Electrochemical Supercapacitors (ES), also known as Supercapacitor or Ultracapacitor, has been regarded as an advanced electrical energy storage device for decades. Fabrication of advanced electrode materials is of critical importance for advanced ES. Among various materials used for ES electrode, polypyrrole (PPy) is found to be a promising material due to high specific capacitance, good electrical conductivity, low cost and ease of processing. The use of advanced anionic dopants and addition of multiwall carbon nanotube (MWCNT) have been proved an .effective approach towards advanced PPy based ES with improved electrochemical behaviors.
In this research, chemical polymerization of PPy powders and PPy/MWCNT composite materials have been successfully accomplished in presence of advanced anionic dopants, including chromotrope families, amaranth, pyrocatechol violet, eriochrome cyanine R and acid fuchsin. The influence of polyaromatic dopants with different molecular size, charges and charge to mass ratios on the microstructure and electrochemical characteristics has been discussed. PPy coated MWCNT with uniform microstructures was successfully achieved in simple chemical methods.
The results showed PPy powders with enhanced microstructures and electrochemical behaviors can be obtained by using such advanced anionic dopants. Multi-charged polyaromatic dopants with larger molecular size benefitted PPy powders with smaller particle size, improved specific capacitance, and enhanced cycling stability, at high electrode mass loadings. Moreover, advanced aromatic dispersant and chemical synthesis was proved a simple and effective method for fabrication of PPy/MWCNT composite materials at different PPy/MWCNT mass ratio, among which the powder with PPy/MWCNT mass ratio of 7:3 showed optimum electrochemical performance. Last but not the least, the use of advanced high porosity current collector (Ni foam) allowed high electrode mass loading and good electric conductivity. As a result, advanced PPy/MWCNT composite materials which allows improved electrochemical behaviors, especially at high mass loading, are promising electrode materials for ES. / Thesis / Master of Applied Science (MASc)
| Identifer | oai:union.ndltd.org:mcmaster.ca/oai:macsphere.mcmaster.ca:11375/16040 |
| Date | 11 1900 |
| Creators | Zhu, Yeling (Yale) |
| Contributors | Zhitomirsky, Igor, Materials Science and Engineering |
| Source Sets | McMaster University |
| Language | English |
| Detected Language | English |
| Type | Book, Thesis |
Page generated in 0.0021 seconds