An iodine surface layer has been prepared on Ru(poly) and Ru(0001) electrodes by exposure to iodine vapor in UHV and polarizing in a 0.1 M HClO4/0.005 M KI solution, respectively. A saturation coverage of I on a Ru(poly) electrode passivates the Ru surface against significant hydroxide, chemisorbed oxygen or oxide formation during exposure to water vapor over an electrochemical cell in a UHV-electrochemistry transfer system. Immersion of I-Ru(poly) results in greater hydroxide and chemisorbed oxygen formation than water vapor exposure, but an inhibition of surface oxide formation relative that of the unmodified Ru(poly) surface is still observed. Studies with combined electrochemical and XPS techniques show that the iodine surface adlayer remained on top of the surface after cycles of overpotential electrodeposition/dissolution of copper on both Ru(poly) and Ru(0001) electrodes. These results indicate the potential bifunctionality of iodine layer to both passivate the Ru surface in the microelectronic processing and to act as a surfactant for copper electrodeposition. The electrodeposition of Cu on Ru(0001) or polycrystalline Ru was studied using XPS with combined ultrahigh vacuum/electrochemistry methodology (UHV-EC) in 0.1 M HClO4 with Cu(ClO4)2 concentrations ranging from 0.005 M to 0.0005 M, and on polycrystalline Ru in a 0.05M H2SO4/0.005 M CuSO4/0.001 M NaCl solution. The electrochemical data show well-defined cyclic voltammograms (CV) with a Cu underpotential deposition (UPD) peak and overpotential deposition (OPD) peak. XPS spectra of Ru electrodes emersed from perchloric acid solution at cathodic potentials indicate that ClO4- anions dissociate to yield specifically adsorbed Cl and ClOx species. Subsequent Cu deposition results in the formation of a thin, insoluble Cu(II) film with Cu(I) underneath. In contrast, similar deposition on polycrystalline Ru in the sulfuric acid/Cu sulfate solution with NaCl added yields only Cu(0), indicating that the formation of Cu(II) and Cu(I) involves both Cl and perchlorate interactions with the deposited Cu. A pre-adsorbed layer of iodine on the Ru(0001) surface inhibits perchlorate dissociation in iodide-free electrolyte and leads to the deposition of Cu(0) in the perchlorate bath. XPS depth profile analysis demonstrates that the iodine monolayer "floats" on top of the deposited film, in agreement with previous results, effectively protecting the Cu film from air oxidation.
Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc5577 |
Date | 08 1900 |
Creators | Lei, Jipu |
Contributors | Kelber, Jeffry A., Golden, Teresa D., Marshall, Paul, 1960-, Kaufman, Michael, Wallace, Robert M. |
Publisher | University of North Texas |
Source Sets | University of North Texas |
Language | English |
Detected Language | English |
Type | Thesis or Dissertation |
Format | Text |
Rights | Use restricted to UNT Community (strictly enforced), Copyright, Lei, Jipu, Copyright is held by the author, unless otherwise noted. All rights reserved. |