In the global search for renewable sources of energy, hydrogen is a promising candidate in transportation and electronic applications. Carbon nanotubes (CNTs) have the largest hydrogen storage capacity among the hydrogen storage materials known at present. The Ni-MH battery can be used to store and then discharge large amounts of hydrogen reversibly by using hydrogen storage materials as negative electrode. The electrochemical hydrogen storage performances of metal hydride electrodes with different levels of multi wall carbon nanotubes (20%, 15%, 10%, 5% and 2% of Ni-MH battery's active materials) has been investigated under similar charge-discharge conditions. Electrochemical test cell consisted of a single hydrogen storage negative electrode sandwiched between two NiOOH/Ni(OH)2 positive electrodes. A 6M aqueous KOH solution was used as electrolyte. Electrochemical properties such as specific discharge capacity, high rate charge-discharge capability and cycle life stability have been investigated. The morphology and structure of negative electrode material were examined by scanning electron microscopy, transmission electron microscopy and X-ray diffraction analysis. Chemical analysis of the hydrogen storage alloy was performed using electron probe microanalysis, electron diffraction spectroscopy and induced coupled plasma spectroscopy analysis. Hydrogen absorption-desorption properties were measured in terms of pressure-composition-isotherm curves. It has been found in this study that the presences of CNTs significantly enhanced the overall electrochemical properties of the Ni-MH battery. Maximum specific discharge capacity was observed for 5% CNTs electrode reaching 243 mAh/g, whereas 0% CNTs could only reach 229 mAh/g. High rate charge and discharge capabilities of 5% CNTs electrodes were ~ 241% and 250% higher than the corresponding values for 0% CNTs electrode. Furthermore, the differences in electrochemical hydrogen storage of CNTs with different diameters of 10-20 nm, 20-40 nm, 40-60 nm, and 60-100 nm were investigated. Electrochemical results demonstrated that CNTs with different diameters showed a large variation in the electrochemical hydrogen storage capability under the similar experimental condition. A comparison between electrodes with different CNTs studies was carried out in order to optimize nanotubes choices for Ni-MH battery. It was found that smaller tube diameters, 20-40 nm and 5% CNTs negative electrode showed the best electrochemical properties of Ni-MH battery system.
Identifer | oai:union.ndltd.org:ADTP/234855 |
Date | January 2006 |
Creators | Sultana, Humara, Materials Science & Engineering, Faculty of Science, UNSW |
Publisher | Awarded by:University of New South Wales. School of Materials Science and Engineering |
Source Sets | Australiasian Digital Theses Program |
Language | English |
Detected Language | English |
Rights | Copyright Humara Sultana, http://unsworks.unsw.edu.au/copyright |
Page generated in 0.0015 seconds