We have fabricated nanofuses from thin-film, arc-evaporation carbon for use in permanent data storage. Thin film carbon fuses have fewer fabrication barriers and retain the required resistivity and structural stability to work as a data storage medium. Carbon thin films were characterized for their electrical, microstructural, and chemical bonding properties. Annealing the thin-film carbon in an argon environment at 400°C reduced the resistivity from about 4*10-2 Ω cm as deposited down to about 5*10-4 Ω cm, allowing a lower blowing voltage. Nanofuses with widths ranging from 200 nm down to 60 nm were fabricated and tested. They blow with voltages between 2 V and 5.5 V, and the nanofuses remain stable in both a "1" and a "0" state under a constantly applied read voltage of 1 volt for over 90 hours, corresponding to a cumulative time of >1012 reads.
| Identifer | oai:union.ndltd.org:BGMYU2/oai:scholarsarchive.byu.edu:etd-7793 |
| Date | 01 April 2018 |
| Creators | Laughlin, Kevin Robert |
| Publisher | BYU ScholarsArchive |
| Source Sets | Brigham Young University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | All Theses and Dissertations |
| Rights | http://lib.byu.edu/about/copyright/ |
Page generated in 0.0024 seconds