The electronic g-tensor in antimony doped cadmium sulphide has been measured at 1.1°K. A sample doped to a room temperature resistivity of 3.3 ohm-cm exhibited an anisotropic g-tensor with g// = 1.788 and g⊥ = 1.770.
A single asymmetric line was observed. The asymmetry of this line was found to decrease with decreasing incident power. Further experiments to study this line shape are indicated. / Science, Faculty of / Physics and Astronomy, Department of / Graduate