This master thesis deals with surface hardening of steels, especially with rotary flash hardening of 42CrMo4 steel (WNr 1.3563, ČSN 15142). In this method homogenous heating of whole surface occurs during a very fast rotation of the component. In the theoretical part of this thesis the most common methods of surface hardening are described, with focus on laser and electron beam technologies. In the experimental part special device for this application was constructed. Rotary flash hardening was done using different radiation source and experimantal device parameters. The hardened surface layer of maximal thickness of 0,7 mm and width of 5,6 mm was achieved using laser beam. Results with electron beam were way better, because this technology allows to control the distribution of power along the beam width in order to improve the width/thickness ratio of hardened layer. Using this method maximal layer thickness of 1,4 mm and width of 13,4 mm was achieved.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:400861 |
Date | January 2019 |
Creators | Klusáček, Martin |
Contributors | Jan, Vít, Kouřil, Miloslav |
Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0014 seconds