Studies of oxide desoption from GaAs by diffuse electron scattering and optical reflectivity

We have determined that the temperature for desorption of gallium oxide from GaAs increases linearly with oxide thickness, for oxide layers between about 6Å and 26Å thick. The temperature for the oxide desorption ranged from 580°C to 630°C. The wafer temperature was determined from the optical band-gap measured from the diffuse reflectivity of the sample, which was polished on the front surface and textured on the back surface. Different thicknesses of oxide layers were created by varying the exposure time of the GaAs wafers to a low pressure oxygen plasma. The oxide thicknesses were determined by XPS analysis. Desorption experiments were carried out in a VG V80H MBE system under a As4 beam equivalent pressure of 1.5 x 10⁻⁵ ton.
Measurement of diffuse light scattering using a HeNe laser shows an abrupt and non-reversible increase in the scattered light intensity during the oxide desorption. This suggests the surface is macroscopically roughened due to inhomogeneous desorption of the oxide.
The oxide desorption was also studied by monitoring the secondary electrons produced by the high energy electrons from the RHEED gun. After the gallium oxide desorption there is a reversible, order of magnitude, increase in the number of scattered electrons produced by the incoming primary beam. We interpret this result as evidence for some form of microscopic roughening. / Science, Faculty of / Physics and Astronomy, Department of / Graduate

Identiferoai:union.ndltd.org:UBC/oai:circle.library.ubc.ca:2429/30416
Date January 1991
CreatorsVan Buuren, Anthony W.H.
PublisherUniversity of British Columbia
Source SetsUniversity of British Columbia
LanguageEnglish
Detected LanguageEnglish
TypeText, Thesis/Dissertation
RightsFor non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use.

Page generated in 0.0018 seconds