Příprava a vlastnosti dopovaných piezokeramických materiálů na bázi BaTiO3 / Fabrication and properties of doped piezoceramics based on BaTiO3

This diploma thesis deals with the preparation of doped piezoceramic materials based on BaTiO3 using electrophoretic deposition. Five rare earth oxides, i.e. Er2O3, Dy2O3, Eu2O3, Tb407 and CeO2, were used as dopants in amounts of 1, 3, and 5 wt. %. The prepared deposits were evaluated in terms of preparation methodology, high temperature dilatometry, X-ray diffraction analysis, relative density, mean grain size, hardness and fractographic analysis. The study of dilatometric curves described the sintering behavior and its changes at different material compositions. X-ray diffraction analysis revealed a tetragonal phase in all samples; the tetragonality of the BaTiO3 crystalline cell decreased with dopant content. By a suitable choice of dopant, it was possible to significantly increase the relative density of sintered samples, their hardness and at the same time prevent the samples from coarsening of the microstructure during heat treatment. A relative density up to 98 %, a mean grain size below 1 m and a hardness of over 10 GPa were achieved. Analysis of the fracture surfaces revealed that the fracture mode was transcrystalline for the most of studied materials; only the samples doped with cerium dioxide had fracture surfaces with both transcrystalline and intercrystalline fracture modes. Based on the obtained results, a suitable composition of the material for the intended use in a layered piezoceramic harvester was identified, which, in addition to the BaTiO3 layers, consists of functionally-protective Al2O3 and ZrO2 layers.

Identiferoai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:417065
Date January 2020
CreatorsMařák, Vojtěch
ContributorsChlup, Zdeněk, Drdlík, Daniel
PublisherVysoké učení technické v Brně. Fakulta strojního inženýrství
Source SetsCzech ETDs
LanguageCzech
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/masterThesis
Rightsinfo:eu-repo/semantics/restrictedAccess

Page generated in 0.0016 seconds