Multiple step tests under cyclic strain control have been performed using cylindrical specimens of cast polycrystalline Inconel 738LC superalloy at 23, 700, 500, 800 and 900 °C in laboratory atmosphere to obtain cyclic stress-strain curves. During cyclic straining of specimen were obtained cyclic hardening-softening curves. Their progress changed with temperature and strain amplitude. Evaluated cyclic stress-strain curves are shifted to lower stresses with increasing temperature. Surface relief was observed in fatigued specimens under SEM and metalography under optic microscopy. Slip markings were studied on specimen surface fatigued at 700 °C .Stress-strain response is compared and discussed in relation to the surface observations - persistent slip markings.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:228279 |
| Date | January 2008 |
| Creators | Šmíd, Miroslav |
| Contributors | Obrtlík, Karel, Petrenec, Martin |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0022 seconds