SODIUM HYPOCHLORITE'S EFFECT ON NICKEL-TITANIUM ROTARY INSTRUMENTS AND ITS EFFECT ON RESISTANCE TO FRACTURE

The purpose of this study was to examine the effect of partial and total immersion in sodium hypochlorite on nickel-titanium rotary files and to determine whether resistance to fracture was influenced by the immersion time. One hundred K3™ and 100 ProFile® rotary files were either partially or totally immersed in 5.25% sodium hypochlorite for zero, one, five, thirty, or sixty minutes. After immersion, files were subjected to cyclic fatigue testing. Time to fracture was recorded and analyzed by a two-way ANOVA. Tukey's honest significant difference was used to identify any differences in immersion times. Within all ProFile groups and partial immersion K3 groups, there was no significant decrease in time to fracture with increased immersion time in sodium hypochlorite. Only the K3 total immersion groups revealed a significant decrease in time to fracture with increased immersion time in sodium hypochlorite.

Identiferoai:union.ndltd.org:vcu.edu/oai:scholarscompass.vcu.edu:etd-1940
Date01 January 2007
CreatorsSmith, Michael Shane
PublisherVCU Scholars Compass
Source SetsVirginia Commonwealth University
Detected LanguageEnglish
Typetext
Formatapplication/pdf
SourceTheses and Dissertations
Rights© The Author

Page generated in 0.0018 seconds