Estudo da degradação de ponteiras de endoscópios utilizadas em endoscopia digestiva alta. / Study of the degradation of endoscopes tips used in upper digestive endoscopy.

Submitted by Johnny Rodrigues (johnnyrodrigues@ufcg.edu.br) on 2018-04-17T12:25:43Z
No. of bitstreams: 1
ANTÔNIO AUGUSTO FRAGA DE ANDRADE - DISSERTAÇÃO PPG-CEMat 2014..pdf: 2871535 bytes, checksum: c0965a012ab765af77feb84c2c22a016 (MD5) / Made available in DSpace on 2018-04-17T12:25:43Z (GMT). No. of bitstreams: 1
ANTÔNIO AUGUSTO FRAGA DE ANDRADE - DISSERTAÇÃO PPG-CEMat 2014..pdf: 2871535 bytes, checksum: c0965a012ab765af77feb84c2c22a016 (MD5)
Previous issue date: 2014-12-18 / O aparelho endoscópico utilizado atualmente para estudo do trato gastro-intestinal (o
video-endoscópio) é resultado de quase 200 anos de evolução tecnológica. Estes
endoscópios não podem ser esterilizados pelos métodos clássicos. Por sua
complexidade, o processo de limpeza e desinfecção de endoscópios não é somente
uma preocupação da enfermagem, ela se tornou multidisciplinar, pois exige
discussão sobre riscos físicos, biológicos e químicos, tanto para o paciente quanto
para a equipe. A borracha da ponta flexível dos endoscópios é uma peça
fundamental para a preservação da vedação do endoscópio e principalmente
preservação do paciente. Esta borracha sofre desgaste tanto durante o exame como
pelos processos de desinfecção do equipamento que acabam agredindo a superfície
do material. O seu desgaste ou ruptura pode acarretar na queima do gerador de
imagem. A troca da borracha da ponta é considerada uma manutenção parcial e
deve sempre ser executada periodicamente. Baseado no exposto este trabalho teve
como objetivo principal estudar e avaliar a degradação ocorrida em ponteiras
flexíveis de endoscópios digestivos submetidos a procedimentos médicos. Como
resultados pode-se verificar nas microscopia, tanto ótica como eletrônica, morfologia
rugosa com presença de poros para a ponteira virgem, nas ponteiras utilizadas por
diferentes períodos de tempo verificou-se intensificação destas rugosidades. Por
DRX pode-se observar um perfil praticamente amorfo típico de elastômero, além de
identificar a presença de compostos de carga no polímero. Por FTIR pode-se
comprovar diferentes estruturas para as amostras estudadas, levando a crer que
algumas possuem polidimetilsiloxana em excesso com relação ao fluorelastômero.
Por EDS pode-se verificar a exteriorização de compostos presentes no interior do
elastômero após o período de degradação. No ensaio de tração foi verificada
diminuição das propriedades físicas do elastômero devido a degradação ocorrida.
No ensaio de ângulo de molhabilidade verificou-se que mesmo após o processo de
degradação todas as amostras ainda apresentavam-se hidrofóbicas. Em síntese,
este trabalho observou a necessidade de se desenvolver um material específico
para utilização como ponteiras de endoscópios, já que os existentes no mercado
aparentemente não tem destino especifico para aplicações biológicas. Ou seja,
mesmo em sua forma virgem o elastômero em questão já apresenta fatores que não
tornam sua utilização em meio biológico tão viável. / The endoscopic device currently used to study the gastrointestinal tract (the videoendoscope)
is the result of nearly 200 years of technological evolution. These
endoscopes can not be sterilized by the classical methods. Due to its complexity, the
process of cleaning and disinfection of endoscopes is not only a concern of nursing,
she became multidisciplinary, since it requires discussion of physical, biological and
chemical hazards, both for the patient and for the team. The flexible rubber tip of the
endoscope is a key piece to preserve the seal of the endoscope and especially
preservation of the patient. This rubber wears out both during the test as the
disinfection of equipment that processes attacking the end surface of the material.
Your wear or breakage may result in the image generator burns. The replacement of
the rubber tip is considered a partial maintenance and must always be performed
periodically. Based on the above this work aimed to study and evaluate the
degradation occurred in flexible tips of digestive endoscopes undergoing medical
procedures. The results can be seen in microscopy, both optical and electronic,
rough morphology with the presence of pores to the virgin tip, the tips used for
different periods of time there was intensification of these ridges. XRD can observe
typical listing a substantially amorphous elastomer, and identify the presence of
compounds in the polymer charge. FTIR can prove different structures for the studied
samples, leading to the belief that some have polydimethylsiloxane in excess with
respect to the fluoroelastomer. EDS can verify the externalization of compounds
within the elastomer after the degradation period. In the tensile test was observed
decrease in physical properties of the elastomer due to degradation occurred. On
test wetting angle was found that even after the degradation process all the samples
still had become hydrophobic. In summary, this study observed the need to develop
a specific material for use as tips of endoscopes, since on the market apparently has
no specific target for biological applications. That is, even in its virgin form the
elastomer in question already has factors that do not make their use in biological
environment as possible.

Identiferoai:union.ndltd.org:IBICT/oai:localhost:riufcg/399
Date17 April 2018
CreatorsANDRADE, Antônio Augusto Fraga de.
ContributorsMENEZES, Romualdo Rodrigues., FOOK, Marcus Vinícius Lia., BARBOSA, Rossemberg Cardoso., LIMA, Rodrigo José da Silva.
PublisherUniversidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0022 seconds