A method for the synthesis of submicron copper coated polystyrene particles by electroless deposition has been developed. In this technique, the carboxylated and sulfated polystyrene latex particles of 0.1 μm and 0.24 μm diameter, are first activated by conditioning in a solution of tetraammine palladium (II) chloride monohydrate and then plated in an electroless bath containing cupric sulfate, EDTA-disodium salt, some stabilizers and basic formaldehyde at 72 ± 1°C. The interaction between carboxylic acid groups and Pd(NH₃)₄Cl₂.H₂O has been studied using uv spectroscopy. Copper coated carboxylated polystyrene particles with a mean diameter of 0.4 μm and a standard deviation of 9% of the mean diameter have been synthesized. The size, shape and purity of these particles have been determined by SEM, EDX, and ESCA analysis. The microcrystallinity of the particles has been determined by XRD technique.
Identifer | oai:union.ndltd.org:arizona.edu/oai:arizona.openrepository.com:10150/277911 |
Date | January 1991 |
Creators | Chowdhury, Rina, 1965- |
Contributors | Raghavan, Srini |
Publisher | The University of Arizona. |
Source Sets | University of Arizona |
Language | en_US |
Detected Language | English |
Type | text, Thesis-Reproduction (electronic) |
Rights | Copyright © is held by the author. Digital access to this material is made possible by the University Libraries, University of Arizona. Further transmission, reproduction or presentation (such as public display or performance) of protected items is prohibited except with permission of the author. |
Page generated in 0.0009 seconds