The diploma thesis describes the influence of humid conditions on the curing of epoxy resins by multifunctional amines. The aim of the experimental part was the identification of degradation products and their quantification, as well as the determination of the influence of humid conditions on the degree of hardening, modulus of elasticity, and flexural strength. Another goal was to optimize the formulation of the reactive mixture for the preparation of epoxy resin with lower susceptibility to carbamate bloom. The degradation products were evaluated by determining the mechanical properties by bending test according to the standard ČSN EN 179-1. The degree of hardening was monitored through temperature modulated differential scanning calorimetry (TMDSC). Degradation products were identified by Fourier transform infrared spectroscopy (FTIR) and quantified by UV-VIS spectroscopy. The morphology of the surface layer was monitored by confocal laser scanning microscopy (CLSM). The dependence of the relative humidity of the environment on the curing process of the epoxy resin and its resulting mechanical properties was determined. Based on the analyzes, a modification of the formulation for the suppression of spurious carbamate during the curing of the epoxy matrix was designed and experimentally verified.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:449707 |
| Date | January 2021 |
| Creators | Švardala, Daniel |
| Contributors | Tocháček, Jiří, Petruš, Josef |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0019 seconds