The thermal conductivities of foamed polymer based materials are much lower thermal conductivity values than unfoamed polymeric materials. Especially, thermal conductivity values of foamed polymers with closed-cell structure decreases to 0.03
W/m.K. The reinforcement of foamed polymeric materials by mixing with bitumen lowers the raw material cost.
The main objective of this study is to make a new thermal insulation material with low thermal conductance. In this study, the effects of concentration of calcium carbonate as inorganic filler and the effects of cross-linking on the properties foamed and unfoamed ethylene-vinyl acetate (EVA) copolymer based bituminous blends and composites were investigated. Applications such as thermal, mechanical characteristics of foamed and unfoamed EVA based bituminous composites were investigated.
Foamed EVA based bituminous composites were prepared by using Brabender Plastic Coder, PLV 151. Mixing was made at 120 º / C at 60 rpm for 15 minutes. The prepared blends were molded by a technique called Hand Lay-up Self-expanding Batch Molding (HLUSEBM) which was firstly applied by our group. The molding temperature was 170 º / C at which chemical blowing agent and cross-linking agent decomposes.
According to test results, at moderate chemical blowing agent and EVA content, the best closed-cell structure with high porosity and low thermal conductivity values were obtained. The compressive properties of foamed polymer based bituminous composites (FPBBCs) increase with increasing CBA and EVA content.
With increasing calcium carbonate and EVA concentration, the porosity of FPBBCs increases but thermal conductivity of them decreases. On the other hand, with increasing filler content but with decreasing EVA concentration elastic modulus of FPBBCs increases but elastic recovery decreases.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/3/12610215/index.pdf |
| Date | 01 January 2009 |
| Creators | Cankaya, Burhan Fuat |
| Contributors | Bayramli, Erdal |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for public access |
Page generated in 0.002 seconds