Properly proportioned, placed and cured concrete can be durable under most conditions. However, deterioration of concrete does occur under certain environments. One of the problems that affect the durability of hardened concrete is delayed ettringite formation (DEF) which is an important problem encountered in precast concrete industry where high temperature curing is applied. Although there had been many researches on DEF, there are still many uncertainties about its chemistry and mechanism.
In this study, the effects of partial cement replacement by different mineral admixtures (trass, blast furnace slag and fly ash), SO3/Al2O3 molar ratio and specific surface area of cement on DEF were investigated. For this purpose, 9 groups of control cements were prepared with 3 different specific surface areas and 3 different SO3/Al2O3 molar ratios. Different amounts of mineral admixtures were blended with the control cements. High temperature curing was applied to the cement pastes and the expansions of these pastes were measured periodically for 240 days.
v
The experimental results obtained were interpreted for a comparative analysis of the effects of the afore-mentioned parameters.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12612494/index.pdf |
| Date | 01 September 2010 |
| Creators | Topbas, Selim |
| Contributors | Tokyay, Mustafa |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for public access |
Page generated in 0.0019 seconds