SÃntese e caracterizacÃes de nanopartÃculas de FeCo/(Fe,Co)304 com acoplamento magnÃtico tipo exchange spring sintetizadas pelo mÃtodo sol-gel Proteico. / Synthesis and characterization of FeCo/(Fe,Co)3O4 nanoparticles with magnetic couplings synthesized by Sol-gel protein method

Conselho Nacional de Desenvolvimento CientÃfico e TecnolÃgico / NanopartÃculas de FeCo recobertas com (Fe,Co)3O4 (Magnetita dopadas com cobalto) na estrutura casca caroÃo (Core-Shell), foram sintetizadas pela rota quÃmica conhecida como Sol-Gel Proteica. Os materiais sintetizados foram caracterizados por Termogravimetria (TG), DifraÃÃo de Raios-X (DRX), Magnetometria de Amostra Vibrante (VSM), Espectroscopia MÃssbauer, Microscopia EletrÃnica de Varredura (MEV) e Microscopia EletrÃnica de TransmissÃo (MET). Os resultados mostram que o aumento da temperatura de re-oxidaÃÃo influi diretamente no tamanho da casca (Shell) bem como o aumento da razÃo entre a magnetizaÃÃo remanente pela magnetizaÃÃo de saturaÃÃo. O efeito de Exchange Spring e Exchange Bias foram observados nas curvas de histerese. A estrutura Core-Shell foi formada de maneira nÃo homogÃnea, ou seja, nem todas as partÃculas foram recobertas pela magnetita. / FeCo Nanoparticles coated with (Fe,Co)3O4 (Magnetite doped with cobalt) were synthesized by the chemical route known as Sol-Gel Protein. The synthesized materials were characterized by thermogravimetry (TG), X-Ray Diffraction (XRD), Vibrating Sample Magnetometry (VSM), MÃssbauer spectroscopy, Scanning Electronic Miscroscopy (SEM) and Transmission Electronic Microscopy (TEM). The results show that the increase in temperature directly influences the size of the shell (Shell) and increased the ratio of remanent magnetization to the saturation magnetization. The effect of Exchange Spring and Exchange Bias were observed in the hysteresis curves. The Core-Shell structure was formed a non-homogeneous manner, ie not all the magnetite particles were coated.

Identiferoai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:10479
Date21 December 2015
CreatorsDiego FÃlix Dias
ContributorsJose Marcos Sasaki
PublisherUniversidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em FÃsica, UFC, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Formatapplication/pdf
Sourcereponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0023 seconds