_Dissertação de Jeferson. Final.pdf: 4272091 bytes, checksum: f4331385778a225310976db01ea0733b (MD5) / CAPES / Nanocompósitos híbridos inéditos compostos por nanofitas de óxido de
vanádio/polipirrol e óxido de vanádio/politiofeno, foram preparados aplicando
ultrassom de alta-intensidade durante um período de 6 horas. Nanocompósitos são
materiais em que os componentes interagem em nível molecular, permitindo com isso
o surgimento de novas propriedades, fruto do sinergismo proporcionado pela
combinação dos precursores. Os precursores dos nanocompósitos utilizados nessa
dissertação foram o pentóxido de vanádio cristalino (c-V2O5), que possui uma
estrutura lamelar capaz de acomodar outras espécies, e os monômeros de pirrol e
dímeros de 2,2-bitiofeno, que são oxidados pelo c-V2O5 e polimerizam no interior do
mesmo. Seis amostras de cada monômero foram preparadas mantendo-se a
quantidade de c-V2O5 constante e variando o número de mols dos monômeros. As
técnicas de difração de raios-X (DRX), espectroscopia de infravermelho com
transformada de Fourier (FT-IR), análise elementar de carbono, hidrogênio, nitrogênio
e enxofre, análise termogravimétrica (TGA) e microscopia eletrônica de varredura
(MEV) foram utilizadas para caracterizar os materiais produzidos. A análise conjunta
das técnicas de investigação mostrou a formação de materiais fibrilares (largura média
de 40,0 nm) em que o polímero se encontra inserido nas lamelas do óxido, acarretando
numa uma expansão média de 10,0 Å. A composição dos materiais tratados
sonoquimicamente foi determinada com o auxílio das medidas de TGA e análise
elementar. As imagens de MEV indicaram que a morfologia do material final é fibrilar.
Assim, um mecanismo de formação dos fibras híbridas foi proposto com o objetivo de
explicar a morfologia fina / Hybrid nanocomposites consisting of the nanoribbons polypyrrole/vanadium oxide
and polythiophene / vanadium oxide have been prepared by applying high-intensity
ultrasonic during a period of 6 hours. The nanocomposites are characterized as
materials in which the components interact at the molecular level, thereby allowing
the emergence of new properties, due to the synergy provided by the combination of
precursors. The precursors of nanocomposites used in this dissertation are crystalline
vanadium pentoxide (c-V2O5), which has a lamellar structure capable of
accommodating other species and monomers pyrrol and 2,2-bithiophene, which are
oxidized by c-V2O5 and polymerize inside the same. Six samples of each monomer
were prepared by keeping the amount of c-V2O5 constant and varying the number of
moles of the monomers the pyrrole and 2,2-bithiophene. Techniques of X-ray
diffraction (XRD), infrared spectroscopy with Fourier transform (FT-IR), elemental
analysis of carbon, hydrogen, nitrogen and sulfur, thermogravimetric analysis (TGA)
and scanning electron microscopy (SEM) were used to characterize the materials
produced. The joint analysis of the technical investigation showed the formation of
fibrillar material (average width of 8.0 nm) in which the polymer is inserted in the
lamella oxide with an average increase of 10.0 Å. The composition of sonochemically
treated materials were determined with the aid of the measures TGA and elemental
analysis. The SEM images showed that the morphology of the final material is fibrillar.
Thus, a mechanism for the formation of hybrid fibers was proposed in order to explain
the final morphology.
| Identifer | oai:union.ndltd.org:IBICT/oai:192.168.11:11:ri/16251 |
| Date | 09 1900 |
| Creators | Almeida, Jeferson do Rosário |
| Contributors | Santos, Marcos Malta dos, Boaventura Filho, Jaime Soares, Dall'Antonia, Luiz Henrique |
| Publisher | Instituto de Química, Química, UFBA, brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFBA, instname:Universidade Federal da Bahia, instacron:UFBA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds