Orientador: Paulo Roberto Mei / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-12T11:09:37Z (GMT). No. of bitstreams: 1
Bubani_FrancodeCastro_M.pdf: 7334881 bytes, checksum: 9cc4f96ceff0972bc2552404b4ccee84 (MD5)
Previous issue date: 2008 / Resumo: Os efeitos da adição de níquel e da temperatura em ligas ferro-cromo foram estudados. Sete ligas de base ferro, com 18% Cr e teores de níquel variando entre zero e 60%, foram utilizadas no estudo (0, 10, 20, 30, 40, 50 e 60% Ni). Foram realizados ensaios de tração em temperatura ambiente, 350 e 700 ºC; simulação por termodinâmica computacional; microscopia ótica no estado recozido, nas amostras de quick stop, após deformação a frio, a 350 e a 700 ºC; difração de
raios X no estado recozido, após deformação a 350 e a 700 ºC; ensaio de dureza a quente a 100, 200, 300 e 400 ºC; ensaio de impacto Charpy em temperatura ambiente e a -196 ºC; e ensaio de quick stop; análise térmica por DTA; ensaios de dureza no estado recozido, nos cavacos obtidos em torneamento, após deformação a 350 e 700 ºC. Os resultados dos ensaios de tração a 350 ºC foram correlacionados com os dados obtidos por Marques (2007), visando relacionar propriedades mecânicas e usinabilidade. A tendência geral de redução da usinabilidade com o aumento do teor de níquel foi relacionada com o aumento da resistência mecânica e da ductilidade a quente, proporcionados pelo níquel. A alta usinabilidade observada na liga 30% Ni foi relacionada com a presença de inclusões com cálcio nesta liga, o que proporcionou ganhos muito expressivos em usinabilidade, mas sem prejudicar as propriedades mecânicas avaliadas. / Abstract: The effects of nickel addition and temperature in iron-chromium alloys have been studied. Seven iron-base alloys with 18% Cr and nickel content varying from zero to 60% were used in the study (0, 10, 20, 30, 40, 50 and 60% Ni). The alloys were submitted to tension tests at room temperature, 350 and 700 ºC; computational thermodynamics simulations; optical metallography observations in annealed state, after deformation at room temperature, 350 and 700 oC, and in quick stop samples; x-ray diffraction, annealed and after deformation at 350 and 700 ºC; hot hardness test at 100, 200, 300 and 400 ºC; Charpy impact tests at room temperature and at -196 ºC; quick stop test; differential thermal analysis tests; Vickers hardness tests: annealed, on chips, after deformation at 350 and 700 ºC. The results of the tension tests at 350 ºC were correlated with the data obtained by Marques (2007), aiming at reaching a relationship between mechanical properties and machinability. The general tendency of reduction in machinability with the increase of nickel content was related to the increase in mechanical strength and hot ductility provided by nickel. The high machinability observed in the 30% Ni alloy was related with the presence of calcium inclusions in this alloy, which allowed for significant gains in machinability, but without loss to the evaluated mechanical properties. / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263098 |
| Date | 12 August 2018 |
| Creators | Bubani, Franco de Castro |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Mei, Paulo Roberto, 1953-, Diniz, Anselmo Eduardo, Machado, Álisson Rocha |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 112 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0046 seconds