Previous issue date: 2016-03-18 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O propósito deste estudo foi avaliar, in vitro, a influência de remanescente de materiais obturadores endodônticos, após desobturação e preparo para pino, sobre a resistência de união adesiva de pinos de fibra de vidro cimentados. Foram utilizados 60 dentes humanos unirradiculados sem coroa. As raízes foram preparadas pela técnica coroa-ápice com sistema Reciproc. Para obturação, as raízes foram divididas em grupos (n = 10) de acordo com o cimento endodôntico utilizado: SO= sem obturação; GP=guta percha sem cimento; AHP= guta-percha + AHPlus; SLP= guta-percha + Sealapex; IRT= guta-percha + iRoot SP; e ERZ= guta-percha + EndoRez. As raízes foram obturadas pela técnica do cone único. A cimentação dos pinos de fibra de vidro Rebilda n.12 foi realizada com sistema adesivo futurabond DC e cimento Rebilda DC em 10 mm do comprimento da raiz. Após esse período, as raízes foram seccionadas obtendo-se discos de 2 mm de espessura em cada terço da raiz (3 discos por raiz) que foram submetidos ao teste de push out, análise por meio de uma lupa estereoscópica (40x) para identificação através de scores da presença de remanescente de material obturador na luz do canal e avaliação por espectroscopia de energia dispersiva (EDS) para identificação de remanescente de componentes químicos do cimento endodôntico presentes nos túbulos dentinários. Os dados obtidos foram analisados estatisticamente pelos testes de Kruskal Wallis, Qui Quadrado e teste de Anova e Tukey, todos com nível de significância de 5%. Não houve diferença estatística para a resistência adesiva entre os cimentos na região cervical (p = 0,49), media (p = 0,28) e apical (p = 0,09). Os grupos SLP e ERZ apresentaram menos remanescente de material obturador nas regiões cervical (p = 0,045) e apical (p = 0,006). Significantes diferenças de remanescentes de componentes químicos foram observadas na região apical dos grupos AHP, IRT e SLP. Conclui-se que os materiais endodônticos não influenciaram na resistência de união adesiva de pinos de fibra de vidro. / The purpose of this study was to evaluate the influence of remnants endodontic filling material in root canal on the bond strength of fiberglass posts cemented. Sixty single-rooted human teeth were used.Crowns were removed. The roots were prepared by crown-down technique with Reciproc system. For fillings, the roots were divided (n = 10) according to the sealer used: SO- without fillings; GP-gutta-percha without sealer; AHP- gutta-percha + AHPlus; SLP- gutta-percha + Sealapex; IRT-gutta-percha + iRoot SP; ERZ-and gutta-percha + EndoRez. Single cone obturation technique was used. After root canal fillings, the teeth were kept in an oven 37 0C for 7 days. Cementing fiberglass posts Rebilda n.12 was performed with fiber adhesive system Futurabond DC and cement Rebilda DC in 10 mm of root length, getting stored in an oven at 37 0C for 48 h. After this period, roots were sectioned obtaining 1 disc of 2 mm thickness in each third of the root (3 discs per root), this discs were underwent to push out test, analyzed by means of a stereomicroscope (40x) to identify the presence of remnants of filling material in the lumen of the canal, and then evaluated by energy dispersive spectroscopy (EDS) for identification of chemical components remnants sealer present in the dentinal tubules. Datas were analyzed with Kruskal-Wallis test, Chi square test, and also Anova and Tukey test, 5% of significance. There were no significant differences in push-out bond strengths among the different groups in the coronal (p = 0.49), middle (p = 0.28) or apical third (p = 0.09). Sealeapex and EndoRez groups showed significantly less remnants of filling material at coronal (p = 0.045) and apical levels (p = 0.006).Significant differences of chemical components remnants were found in AHP, IRT and SLP groups on apical third. It is concluded that residual endodontic filling material does not influence on the bond strength of fiberglass.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/138113 |
| Date | 18 March 2016 |
| Creators | Vasconcelos, Rafaela Andrade de [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Carvalho, Cláudio Antonio Talge [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 600, 600 |
Page generated in 0.0032 seconds