Previous issue date: 2017-01-26 / CNPQ / Neste trabalho, descrevemos a preparação de filmes finos de PEDOT:PSS que apresentam ganho na condutividade como resultado do pós-tratamento com co-solventes polares (tais como metanol, ácido fórmico e água), no intuito de melhor entender o papel das interações polares no ganho observado na condutividade. Nesse sentido, o papel de processos físicos de tratamento foi também examinado. Os filmes resultantes foram caracterizados por UV-Vis, Raman, MEV, AFM, ângulo de contato e por medidas elétricas DC. Os dados obtidos por espectroscopia Raman mostram que nos filmes tratados com solventes ocorre uma mudança da estrutura benzenóide para uma conformação quinóide nos anéis aromáticos no PEDOT. Isso leva a um aumento da granulosidade das películas de PEDOT-PSS, o que se reflete em um aumento de sua condutividade. Os resultados obtidos mostram que o pós-tratamento com ácido fórmico se apresenta como o mais promissor entre os examinados, uma vez que os filmes correspondentes experimentaram um aumento de 29 vezes na condutividade (de 0,5 S/cm para 14,5 S/cm). Para os outros tratamentos, o ganho foi de apenas 2 vezes para filmes, quando tratados com água, e de 11,4 vezes para filmes tratados com metanol, enquanto que sonificação da solução por 2h leva a um ganho de 2,94 vezes. / In this work, we describe the preparation of PEDOT: PSS thin films that show gain in conductivity as a result of the post-treatment with polar co-solvents (such as methanol, formic acid and water) in order to better understand the role of these polar interactions on the observed gain in conductivity. In this sense, the effect of physical processes of treatment was also examined. The resulting films were characterized by UV-Vis, Raman, MEV, AFM, contact angle and by DC electrical measurements. The data obtained by Raman spectroscopy show that in the solvent-treated films a change of the benzenoid structure to a quinoidial conformation occurs in the PEDOT aromatic rings. This leads to an increase in the granulation of PEDOT-PSS films, which are reflected in an increase in their conductivity. The results show that the post-treatment with formic acid appear as the most promising among those examined, since the corresponding films experienced a 29-fold increase in conductivity (from 0.5 S / cm to 14.5 S / Cm). For the other treatments, the gain was only 2 times when the films were treated with water and 11.4 times for films treated with methanol, while sonification of the solution for 2 hours leads to a gain of 2.94 times.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpe.br:123456789/24632 |
| Date | 26 January 2017 |
| Creators | BARROS, Yuri Alexandre |
| Contributors | http://lattes.cnpq.br/4505138524062254, MELO, Celso Pinto de |
| Publisher | Universidade Federal de Pernambuco, Programa de Pos Graduacao em Fisica, UFPE, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Breton |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPE, instname:Universidade Federal de Pernambuco, instacron:UFPE |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0015 seconds