The fatigue behavior and cyclic deformation of polyether ether ketone (PEEK) subjected to various uniaxial cyclic loading conditions were experimentally investigated. These include constant amplitude and multi-block loading conditions at various frequencies with zero and non-zero mean strains. Under constant amplitude loading, increasing the test frequency generally resulted in longer fatigue lives for PEEK, while a minimal effect of tensile mean strain was observed. For all fatigue tests under fully- reversed multi-block loadings, pre-loading was found to have a significant beneficial effect on PEEK fatigue resistance irrespective to the load sequence. However, no obvious load history and sequence effect on fatigue behavior was observed for pulsating tension block loading tests. Additionally, three models; strain-based, strain-stress-based, and energy-based models, were correlated to the experimental data in this study. The energy approach was found to provide better fatigue life predictions for PEEK under constant and multi-block loadings with various strain ratios and frequencies.
Identifer | oai:union.ndltd.org:MSSTATE/oai:scholarsjunction.msstate.edu:td-3246 |
Date | 09 December 2016 |
Creators | Shrestha, Rakish |
Publisher | Scholars Junction |
Source Sets | Mississippi State University |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | Theses and Dissertations |
Page generated in 0.0015 seconds