Nickel superalloys are used for high-temperature application in energetic and aerospace industry. They are exposed to aggressive environment at high temperatures with the interactions between fatigue and creep processes, high-temperature oxidation, corrosion and erosion. Lifetime extension of such strained parts while increasing the performance of particular machine is possible by applying protective surface coatings. The subject of this work is to investigate the fatigue failure mechanisms of superalloy Inconel 713LC at 800 °C and to compare these mechanisms between material with a protective coating based on Al-Si and material without coating. The location of initiation fatigue cracks, their propagation and the fatigue crack propagation rate in some areas were analyzed by optical microscopy, scanning electron microscopy and confocal laser scanning microscopy. Based on previous research it was found that the application of the coating AlSi has a positive effect on lifetime of alloy Inconel 713LC. These results were confirmed and estimated in the diploma thesis.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:229060 |
| Date | January 2010 |
| Creators | Smékalová, Jana |
| Contributors | Juliš, Martin, Hutařová, Simona |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0018 seconds