janasi_sr_dr_araiq.pdf: 2566763 bytes, checksum: e10173459cbf62287b0478669d7c6ed0 (MD5) / A substituição parcial de íons Fe3+ por pares de íons (Co2+-Ti4+ ou Co2+-Sn4+) na ferrita de bário hexagonal (BaFe12O19) leva a uma substancial diminuição no campo coercitivo (Hc) com uma pequena mudança na magnetização de saturação (Ms), permitindo seu uso em gravação magnética e magneto-óptica de alta densidade. Os diferentes métodos de preparação de ferritas de bário resultam em produtos com propriedades distintas. Neste trabalho, preparou-se BaFe12-2xCoxTixO19 e BaFe12-2xCoxSnxO19 (0,25 £ x £ 1) por coprecipitação, utilizando cloretos dos metais precursores e solução de KOH/K2CO3 como precipitante. Após a secagem, o produto obtido foi calcinado a 950oC por 3h, lavado e seco. Os difratogramas de raios X indicaram a formação da ferrita de bário. As micrografias eletrônicas de varredura mostraram que os pós obtidos apresentam-se na forma de plaquetas hexagonais de 1 a 2mm. As curvas de magnetização das ferritas de bário dopadas mostraram que o campo coercitivo e a remanência diminuem em função do aumento da razão de substituição x. A curva de magnetização da amostra dopada com Co-Ti, com x = 1 é característica de uma ferrita mole, com Hc = 13,5 kA.m-1 (0,17 kOe), Ms = 46,1 emu.g-1 e Mr = 11,0 emu.g-1. Para a amostra dopada com Co-Sn a diminuição de Mr não é significante. Estes resultados mostraram que as propriedades magnéticas das ferritas de bário dopadas obtidas por coprecipitação foram melhoradas, em relação aos dados da literatura para ferrita de bário pura ou dopada. / The partial substitution of Fe3+ ions with pairs of ions (Co2+-Ti4+ or Co2+-Sn4+) in hexagonal barium ferrite (BaFe12O19) leads to a substantial reduction on coercivity (Hc) with only a low change in saturation magnetization (Ms), allowing its use in high density magnetic and magneto-optical recording. Different preparative methods result in barium ferrites with distinguished properties. In this work, BaFe12-2xCoxTixO19 and BaFe12-2xCoxSnxO19 (0.25 £ x £ 1) were prepared by the coprecipitation method using chloride salt precursors and KOH/K2CO3 solution. After drying, the powder was calcinated at 950oC by 3 h, washed and dried. The X ray diffraction patterns indicated the barium ferrite phase formation. The scanning electron micrographs showed that the particles are hexagonal platelike with diameter size ranging from 1 to 2 mm. The magnetization curves of substituted barium ferrites showed that the values of Hc and Mr decrease with the increase of the substitution ratio x. The magnetization curve profile for Co-Ti substituted sample with x =1 is characteristic of a soft ferrite with Hc = 13.5kA.m-1 (0.17 kOe), Ms = 46.1 emu.g-1 and Mr = 11.0 emu.g-1. These results indicated that the magnetic properties of substituted barium ferrites obtained by coprecipitation were improved when compared with the literature data for pure and substituted barium ferrite.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/102592 |
| Date | January 1997 |
| Creators | Janasi, Suzilene Real [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Jafelicci Júnior, Miguel [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 124 f. : |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1 |
Page generated in 0.0017 seconds