In 2003, the European Community Obligation (directive 2003/5C/EC) regulates a maximal value of soluble hexavalent chromium to 0.0002 % (per weight of dry cement). This limitation leads to modifications of the regular Portland cement by using of suitable reduction agents. Therefore, the possibilities of chromium reduction become a very actual topic. The primary goal of this work is a basic research of the ferrous sulphate influence on hexavalent chromium reduction and also its influence on Portland clinker hydration process. The reduction ability was determined by UV/VIS method. The mechanism and ferrous sulphate influence on Portland clinker hydration process was observed by isothermal calorimetry and mechanical strength tests. XRD method, SEM-EDS analysis and Raman microscopy were used for identification of formed hydration products. Study of hydration mechanism occurring in this system was focused on the divergence observations from the regular Portland cement hydration. Pore solution analysis provided significant information about chromium behavior during the hydration process (substitution and releasing). Chromium incorporation into structure of hydration products during the reduction process was also studied in the pure tricalciumaluminate system with targeted Cr6+ content. This work suggests the possible substitution of the trivalent and hexavalent chromium into structure of monosulphate (AFm) phase.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:256551 |
Date | January 2016 |
Creators | Mončeková, Miroslava |
Contributors | Rovnaníková, Pavla, Drábik, Milan, Havlica, Jaromír |
Publisher | Vysoké učení technické v Brně. Fakulta chemická |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/doctoralThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0079 seconds