The fabrication of broadband single-mode Cr-doped silica fibers (SMCDSFs) using the fiber drawing-tower method with the modified rod-in-tube technique is demonstrated for the first time.
A preform was assembled by using the grown Cr:YAG rod as core and the silica tube as cladding. The outer and inner diameters of the silica tube are 20 and 7 mm, respectively. The initial dimension of the Cr:YAG crystal rod had a length of 0.03 m and a diameter of 500 £gm. The Cr:YAG crystal was grown into a diameter of a 290 £gm with a length of 0.12 m by the LHPG method. The SMCDSFs had a 6 £gm core and a 125 £gm cladding. The transmission loss was 0.08 dB/cm at 1550 nm. The far-field pattern measurements indicated the single-mode characteristic when the propagation wavelength was longer than 1310 nm.
In order to solve the interface of core and cladding, a novel rod-in-tube(RIT) perform was employed by inserting the Cr:YAG crystal rod of 0.03m length and 500 £gm diameter into the silica capillary tube, which had the same diameter with the drilled silica rod. The single-mode Cr-doped fibers had successfully been fabricated and the loss had been reduced to 0.03 dB/cm at 1550 nm with a 5 £gm core and a 125 £gm cladding. Furthermore, the SMCDSFs also had the single-mode characteristic when they operated in the optical communication window.
The successful fabrication of SMCDSFs may be one step forward towards the achievement of utilizing the SMCDSFs as ultra-broadband fiber optical amplifiers to cover the bandwidths in the whole 1300 to 1600 nm range of low-loss and low-dispersion windows of silica fibers and a broadband source for enabling high resolution in optical coherence tomography (OCT).
Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0716110-235811 |
Date | 16 July 2010 |
Creators | Lin, Ting-chien |
Contributors | Sheng-Lung Huang, Wood-Hi Cheng, Jau-Sheng Wang, Yi-Chung Huang, Hsin-Hui Kuo |
Publisher | NSYSU |
Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
Language | Cholon |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0716110-235811 |
Rights | campus_withheld, Copyright information available at source archive |
Page generated in 0.0016 seconds