Orientadores: Florencia Cecilia Menegalli, Theo Guenter Kieckbusch / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia de Alimentos / Made available in DSpace on 2018-08-17T20:07:15Z (GMT). No. of bitstreams: 1
SalasValero_LadyMaria_M.pdf: 3009837 bytes, checksum: 312afc75f23ce98ef04627f10c940f8a (MD5)
Previous issue date: 2011 / Resumo: Alginatos são polissacarídeos extraídos de algas pardas que apresentam uma grande gama de aplicações tecnológicas devido a sua conhecida habilidade em formar géis fortes, biodegradáveis e insolúveis em água ao ser reticulado com Ca2+. Biofilmes baseados nesse mecanismo podem ser confeccionados, formando estruturas transparentes e de alta resistência mecânica, mas que exigem considerável quantidade de plastificante para adequar sua flexibilidade. O objetivo deste trabalho foi desenvolver e caracterizar filmes de alginato reticulados com cátions Ba2+, Sr2+ ou Al3+ e seus atributos funcionais foram comparados aos de filmes de alginato de cálcio. Filmes de diferentes espessuras foram elaborados por casting em processo em duas etapas: um protótipo de filme foi inicialmente formado, vertendo alíquotas de uma solução aquosa contendo alginato de sódio, glicerol como agente plastificante e uma pequena quantidade de íons cálcio para promover uma pré-reticulação, em placas quadradas de acrílico e submetidas a secagem a 40°C. A reticulação destes pré-filmes foi complementada por imersão em soluções de cloreto de bário, de estrôncio ou de alumínio. Filmes com diferentes graus de reticulação, e diferentes concentrações de glicerol foram caracterizados em relação a suas propriedades, tais como: aspecto visual, conteúdo de umidade, massa solubilizada, permeabilidade ao vapor de água, intumescimento em água, resistência mecânica à tração, alongamento, observações por microscopia eletrônica de varredura, opacidade e cor. O estudo indica que o cloreto de bário é uma alternativa eficiente como agente reticulante por apresentar rápida e intensa reticulação da camada superficial dos filmes de alginato formando filmes com boas propriedades funcionais, excelente manuseabilidade, e altos valores de alongamento, porém menos transparentes. Filmes reticulados com Sr2+ apresentaram características funcionais superiores aos filmes reticulados com Ca2+ de mesma espessura, exceto quanto à permeabilidade ao vapor d¿água, que foi ligeiramente mais alta. O uso do íon trivalente Al3+, que é pequeno e lábil, como agente reticulante formou filmes densos devido à reticulação em todo o seu volume, exibindo limitados atributos funcionais, sobretudo em relação a flexibilidade, pois sua compacta estrutura tridimensional impedia a incorporação de glicerol / Abstract: Alginates are polysaccharides extracted from brown seaweeds with a large range of technological applications due to their well known ability to form strong gels that are biodegradable and insoluble in water when crosslinked with calcium ions. Films based on this mechanism can be confectioned, forming transparent structures with high mechanical resistance, but require considerable amount of plasticizers in order to become flexible. This work evaluated the development and characterization of alginate films reticulated with Ba2+, Sr2+ or Al3+ and their functional attributes were compared to films of calcium alginate. Prototypes of films with distinct thicknesses were confectioned by casting in a two-step procedure: different aliquots of an aqueous solution containing sodium alginate, glycerol as plasticizer and a small amount of calcium chloride in order to promote a weak crosslinking were poured in Plexiglas square dishes and dried at 40ºC. The crosslinking of these pre-films were further complemented by immersion in solutions containing barium, strontium or aluminum chloride. Films of different degrees of reticulation and different concentration of glycerol were characterized as to visual appearance, water content, swelling degree, soluble mass, water vapor permeability, mechanical resistance to tension and elongation, opacity, color and were also submitted to SEM observation. This investigation selects barium as an excellent alternative crosslinking agent, since it promotes a fast and intense surface reticulation producing films with good physical attributes and handling, due to their high values of elongation. Films reticulated with Sr2+ show slightly better functional properties compared to calcium alginate films of the same thickness. The use of the small and labile trivalent Al3+ ion as reticulant led to very dense structures due to its ability to crosslink the film core. The films formed, however, were brittle due to lack of flexibility, since the tight tridimensional structure hindered the incorporation of glycerol / Mestrado / Engenharia de Alimentos / Mestre em Engenharia de Alimentos
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/256486 |
| Date | 04 April 2011 |
| Creators | Salas Valero, Lady Maria, 1981- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Kieckbusch, Theo Guenter, 1942-, Menegalli, Florência Cecília, 1944-, Lisboa, Antônio Carlos Luz, Yoshida, Cristiana Maria Pedroso |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia de Alimentos, Programa de Pós-Graduação em Engenharia de Alimentos |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 103 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds