Content:
The present work attempts to analyze the surface and physical properties of leathers finished with cationic and anionic finishing chemicals. The contact angles of liquid drops resting on the leather surface have been used to evaluate surface energy, acidity, basicity components of the surface energy, polarity and work of adhesion. Contact angle values have been measured for chrome tanned and conventionally retanned crust and finished leather made by varying pigment and binder combinations. The wettability of finished leather has been correlated with the contact angle values: the higher the contact angle value the lesser is the wetting observed. Complete wetting can be obtained when the contact angle value is zero i.e. the drop of liquid spreads spontaneously on the surface and partial wetting is obtained when the contact angle value is in between 0and 900. Acrylic binders with different film forming properties, protein, polyurethane and butadiene binders have been combined to prepare different finish formulations.The results have been correlated with wet and dry rub fastness, finish adhesion, vamp flexing value, water vapour permeability and water proofness. It has been observed that when the surface of leather is coated with acrylic binder the contact angle value due to polar solvents(water) , non polar solvents(hexadecane) and moderately polar (DMSO) and methyl iodide show that as the thickness of coating increases, the contact angle value decreases for the base coat and sharply increases when top coat is applied. Top coats have the ability to increase the contact angle and they improve the performance properties of leather such as water resistance, fastness, finish adhesion etc. Cationic and anionic finishing formulations have been compared to study their effect in modifying the surface of finished leather based on contact angle values, wet and dry fastness to circular rubbing and water resistance. It has been observed that leathers finished using anionic finishing technique shows better wet rub fastness and water resistance effect compared to cationic finishing technique.
Take-Away:
The effect of number of top coats on water contact angle value were determined ,and the experiment showed that the value were decreased gradually at the beginning of the coat because the top coats are water based so during the coating process the hydrophobic nature of the surface of chrome tanned leather have decreased.
The experimental result from contact angle value showed that coating with pigments and binders have increased the contact angle value compared to the control crust.
It has been observed that leathers finished using anionic finishing technique shows better wet rub fastness and water resistance effect compared to cationic finishing technique.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa:de:qucosa:34412 |
| Date | 05 July 2019 |
| Creators | Wajino, Mishamo, Dhathathreyan, A. D., Kanth, S. V. K. V. |
| Contributors | International Union of Leather Technologists and Chemists Societies |
| Publisher | Verein für Gerberei-Chemie und -Technik e. V., Forschungsinstitut für Leder und Kunststoffbahnen (FILK) gGmbH |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, doc-type:conferenceObject, info:eu-repo/semantics/conferenceObject, doc-type:Text |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | urn:nbn:de:bsz:14-qucosa2-340872, qucosa:34087 |
Page generated in 0.0022 seconds