Orientadores: Fernanda Miori Pascon, Regina Maria Puppin Rontani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-25T06:58:59Z (GMT). No. of bitstreams: 1
Varanda_Thais_M.pdf: 1172292 bytes, checksum: 71c27c4d27c0cb61adf62bbf82fa7e88 (MD5)
Previous issue date: 2014 / Resumo: Lesões de mancha branca são comumente observadas em dentes decíduos (DD) e quando diagnosticadas e tratadas precocemente com diversos materiais que liberam fluoretos, apresentam prognóstico favorável. Os objetivos desta dissertação foram: (1) avaliar quanti-qualitativamente dois tempos de formação de lesões de cárie sub-superficiais (LCSS) em DD; (2) avaliar quanti-qualitativamente o efeito de três vernizes fluoretados: Duraphat®, MI Varnish¿, e Vanish¿ em LCSS de DD. Para o objetivo 1, utilizou-se 20 DD distribuídos em 2 grupos (n=10): 8 e 16h. Foram produzidas LCSS em blocos de esmalte utilizando-se solução desmineralizadora. Profundidade (análise quantitativa) e homogeneidade (análise qualitativa) das lesões foram avaliadas em microscopia de luz polarizada (MLP). Para a profundidade foram realizadas 3 medidas em cada lesão (em µm) e calculou-se a média. Para a homogeneidade as imagens foram classificadas em escores (0=ausência de homogeneidade; 1=homogeneidade). Os dados quantitativos foram submetidos ao teste de normalidade, Shapiro-Wilk e uma vez que não obedeceram à distribuição normal dos dados, estes foram submetidos ao teste de Mann-Whitney. Quanto à profundidade não se observou diferença significativa entre 8 (75,61±41,46) e 16h (104,53±90,00) (p=0,6272). Para a homogeneidade, 8h promoveu formação de 50% de LCSS homogêneas comparada a 100% em 16h (p=0,0149). Para o objetivo 2, utilizou-se 36 DD (n=9). LCSS foram produzidas em blocos de esmalte por 16h. Os materiais foram aplicados e após 7 dias os espécimes foram seccionados e analisados quanto à profundidade das LCSS (em MLP), perda mineral (dureza Knoop) e quantidade de cálcio (Ca) e fósforo (P) (espectroscopia por energia dispersiva - EDS). A profundidade foi calculada conforme descrito anteriormente. Para a dureza Knoop realizou-se três fileiras de 12 impressões (10, 20, 30, 40, 50, 60, 80, 100, 120, 140, 160 e 180 µm) (25g/5s). Valores de dureza Knoop (KHN) foram obtidos e calculou-se a variação do KHN (?S). Para EDS os espécimes foram observados em microscópio eletrônico de varredura e a quantidade de cálcio (Ca) e fósforo (P) foi calculada nas regiões superficiais e sub-superficiais. As imagens obtidas em MLP foram submetidas à análise descritiva. Os dados quantitativos foram submetidos aos testes Shapiro-Wilk, ANOVA e Tukey como teste post-hoc (?=5%). Não foram observadas diferenças significativas entre os grupos em relação à média das profundidades das LCSS analisadas em MLP. Os grupos tratados apresentaram valores médios semelhantes (39,73±14,20 µm; 32,77±11,86 µm; 38,13±9,17 µm, para Duraphat®, MI VarnishTM e VanishTM, respectivamente), diferente numericamente do grupo controle (54,10±34,56 µm). Para a dureza, observou-se que Duraphat® (2022±1071) apresentou a menor perda mineral comparado aos grupos controle (5239±2299), MI VarnishTM (4505±1098) e VanishTM (4431±1512) (p<0,001, p=0,0022 e p=0,0036, respectivamente). Para EDS tanto para Ca, quanto para P, observou-se ausência de interação entre os materiais e regiões estudadas, porém observou-se diferença significativa para a quantidade de Ca entre as regiões (p<0,05). A região superficial apresentou menor quantidade de Ca que a região sub-superficial. Pode-se concluir que: dezesseis horas foi o tempo mais adequado para formação das LCSS em dentes decíduos; os vernizes fluoretados modificados não se mostraram efetivos em reduzir a perda mineral de LCSS em dentes decíduos; Duraphat® foi o material que apresentou maior efetividade em diminuir a perda mineral de LCSS em dentes decíduos / Abstract: White spot lesions are commonly observed in primary teeth (PT) and when early diagnosed and treated using with various materials that release fluoride, they have a favorable prognosis. The aims of this study were: (1) to evaluate quantitatively and qualitatively 2 formation times of subsurface carious lesions (SCL) in PT; (2) to evaluate quantitatively and qualitatively the effect of three fluoride varnishes: Duraphat®, MI Varnish¿, Vanish¿ in SCL of PT. For the first aim, 20 PT were selected and divided into 2 groups (n = 10): 8 and 16h. SCL was produced in enamel blocks using demineralizing solution. Depth (quantitative analysis) and homogeneity (qualitative analysis) of the lesions were evaluated in polarized light microscopy (PLM). For depth lesion determination 3 measurements were performed in each lesion (µm) and the average was calculated. For homogeneity the images were classified into scores (0 = no homogeneity, 1 = homogeneity). Quantitative data were subjected to normality test, Shapiro-Wilk and once did not show normal data distribution; they were subjected to the Mann-Whitney test. Regarding lesion depth no significant difference was observed between 8h (75.61±41.46) and 16h (104.53±90.00) (p=0.6831). For homogeneity, 8h promoted formation of homogeneous SCL in 50% compared to 100% in 16h (p<0.01). For the second aim, 36 PT (n = 9) were selected. SCL were produced in enamel blocks for 16h. The materials were applied and after 7 days the specimens were sectioned and analyzed for the depth of the SCL (PLM), mineral loss (Knoop hardness) and calcium (Ca) and phosphorus (P) (energy dispersive spectroscopy - EDS). For PLM the lesion depth was calculated as described above. For microhardness, three rows with 12 impressions each were performed (10, 20, 30, 40, 50, 60, 80, 100, 120, 140, 160 and 180?m) (25g/5s). Knoop microhardness (KHN) was obtained and calculated the KHN variation (?S). For EDS specimens were observed in a scanning electron microscope and the amount of calcium (Ca) and phosphorus (P) was calculated in surface and sub-surface regions. The images obtained in PLM were subjected to descriptive analysis. Quantitative data were subjected to the Shapiro-Wilk test, ANOVA and Tukey's test as post-hoc (? = 5%). No significant differences were observed between groups in relation to the average depths of the SCL analyzed in PLM. The treated groups had similar mean values (39.73±14.20µm; 32.77±11.86µm; 38.13±9.17µm to Duraphat®, MI VarnishTM and VanishTM, respectively), numerically different from the control group (54.10±34.56µm). For the hardness, it was observed that Duraphat® (2022±1071) had the lowest mineral loss compared to the control (5239±2299), MI VarnishTM (4505±1098) and VanishTM (4431±1512) (p<0.001, p=0.0022 and p=0.0036, respectively). For EDS, both for Ca and P, there was no interaction between materials and regions studied, but there was a significant difference to the amount of Ca between regions (p<0.05). The surface region showed a lower content of Ca that the sub-surface region. It can be concluded that 16 hours was the most appropriate time for the formation of SCL in primary teeth; modified fluoride varnishes they were not effective in reducing SCL mineral loss of in primary teeth; Duraphat® was the material that showed effectiveness to reduce SCL mineral loss of in primary teeth / Mestrado / Odontopediatria / Mestra em Odontologia
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288857 |
| Date | 25 August 2018 |
| Creators | Varanda, Thais, 1978- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Puppin-Rontani, Regina Maria, 1959-, Pascon, Fernanda Miori, 1977-, Gavião, Maria Beatriz Duarte, Borges, Ana Flavia Sanches |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 60 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0031 seconds