One conventional method for studying dislocations uses the Transmission Electron Microscope (TEM), a complex and expensive piece of equipment which requires extensive specimen preparation in order to thin the specimens to electron transparent thickness. Newer High Resolution Electron Backscatter Diffraction (HREBSD) methods of determining geometrically necessary dislocation content via cross-correlation promise to be able to produce estimates of the dislocation density of the sample over a larger area with considerably less preparation time and using a much more accessible instrument. However, the accuracy of the new EBSD technique needs more experimental verification, including consideration of possible changes in the specimen dislocation density due to the different preparation methods. By comparing EBSD and TEM dislocation measurements of Electron Transparent platinum specimens prepared using the Focused Ion Beam (FIB), along with EBSD dislocations measurements of specimens prepared by both FIB and mechanical polishing techniques, this paper seeks to verify the accuracy of the new method and identify any changes in the specimens’ apparent dislocation density caused by the different preparation processes.
Identifer | oai:union.ndltd.org:BGMYU2/oai:scholarsarchive.byu.edu:etd-9115 |
Date | 01 August 2019 |
Creators | Friedbaum, Samuel Searle |
Publisher | BYU ScholarsArchive |
Source Sets | Brigham Young University |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | Theses and Dissertations |
Rights | http://lib.byu.edu/about/copyright/ |
Page generated in 0.0018 seconds