Concreto autoadensÃvel com agregados graÃdos reciclados de concreto / Self-compacting Concrete with Recycled Concrete Coarse Aggregate

CoordenaÃÃo de AperfeiÃoamento de Pessoal de NÃvel Superior / O Concreto AutoadensÃvel (CAA) possui propriedades intrÃnsecas que o distingue do atual concreto convencional. SÃo fatores como capacidade de autoadensamento, grande quantidade de finos e uso obrigatÃrio de aditivo superplastificante que tornam o CAA um material de elevado desempenho, favorÃvel para a durabilidade, sendo considerado uma evoluÃÃo na tecnologia do concreto e propenso a se tornar o concreto convencional do futuro. Por outro lado, o resÃduo originÃrio da prÃpria indÃstria da construÃÃo civil tem despertado sÃrias preocupaÃÃes para a comunidade, pois se trata de um resÃduo de difÃcil descarte e gerado em volumes cada vez mais crescentes, dado o crescimento econÃmico do PaÃs com consequente aumento do poder aquisitivo da populaÃÃo. Sob esta Ãtica, analisou-se o potencial de produÃÃo do CAA com substituiÃÃo do agregado graÃdo natural (AGN) por agregados reciclados oriundos da reciclagem de concreto, chamado de agregado graÃdo reciclado (AGR), nas porcentagens de 0%, 10%, 20% e 30%. Sabendo que o agregado reciclado, em geral, possui caracterÃsticas distintas do agregado natural, a metodologia empregada iniciou com o tratamento do AGR e caracterizaÃÃo fÃsica de todos os agregados (convencionais e reciclados). Efetuou-se, entÃo, o estudo de dosagem para as relaÃÃes a/c de 0,35, 0,45 e 0,55. ApÃs, estudaram-se um total de 12 traÃos de CAA para avaliaÃÃo de suas propriedades no estado fresco e no estado endurecido. Os ensaios no estado endurecido foram: resistÃncia à compressÃo axial aos 28 e 56 dias, mÃdulo de elasticidade aos 56 dias, absorÃÃo de Ãgua por imersÃo aos 28 dias, Ãndice de vazios aos 28 dias, massa especÃfica real aos 28 dias e profundidade de carbonataÃÃo natural aos 200 dias. Procedeu-se ao tratamento estatÃstico dos resultados pela anÃlise de variÃncia (ANOVA) com posterior modelagem matemÃtica e ANOVA do modelo proposto. Ao final, concluiu-se que o alto teor de aditivo superplastificante resultante do estudo de dosagem da relaÃÃo a/c mais baixa pode ter influenciado para a obtenÃÃo de concretos mais trabalhÃveis e menos suscetÃveis à incorporaÃÃo de um agregado mais poroso do que o agregado natural. TambÃm se concluiu que as propriedades dos CAA manufaturados foram afetadas mais significativamente pela relaÃÃo a/c, indicando a possibilidade de substituiÃÃo de maiores teores de AGN por AGR. / The self-compacting concrete (SCC) has intrinsic properties
that distinguish it known
current
conventional concrete.
It is factors like self-compacting capacity, high amount of fines and
mandatory use of superplasticizer that make
the SCC a material of high performance,
favorable to the durability and is considered an evolution in concrete technology and prone to
become the future conventional concrete. On
the other hand, the residue originated in the
construction industry itself has aroused serious concern to the community, because it is a
residue difficult to discard.
It is
generated in ever-increasing
volumes
due to
economic growth
in the country
with con
sequent increase in
power
population's purchasing.
From this
perspective, we analyzed the production of SCC
with replacement of natural coarse aggregate (NCA) for recycled aggregates from
concrete
recycling, called recycled coarse aggregate
(RCA), in the percentages of 0%, 10%, 20% and 30%. Knowing that recycled aggregate, in
general, has distinct characteristics of natural aggregate, the methodology started with the
treatment of RCA
and physical characterization of all
aggregates (conventional and recycled).
Then, it was done the dosage study
with the w/c ratio of 0.35, 0.45 and 0.55. After,
we studied
a total of 12
mixtures
of
SCC to evaluate its properties in fresh and hardened state. The tests in the hardened state were: compressive strength at 28 and 56 days, modulus of elasticity at 56
days, water absorption by immersion
at
28
days,
content of
voids at 28 days, specific
gravity
at 28 days and the depth of
natural
carbonation at
200 days. We
proceeded to
statistical
processing of results by analysis of v
ariance (ANOVA) followed by mathematical modeling
and model‟s ANOVA. Finally, it was concluded that the high content of superplasticizer
results from the
dosage study
of
lower w/c ratio
can be influenced to achieve
concretes
more
workable
and less sensitiv
e to the incorporation of an aggregate more porous than the natural
aggregate. It was also found that the properties of the
SCC
manufactured were affected more
significantly by the w/c ratio, indicating the possibility of substitution of higher levels of
NCA by RCA

Identiferoai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:7940
Date06 June 2012
CreatorsKelvya Maria de Vasconcelos Moreira
ContributorsAntonio Eduardo Bezerra Cabral
PublisherUniversidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em Engenharia Civil Estruturas e ConstruÃÃo Civil, UFC, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Formatapplication/pdf
Sourcereponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0023 seconds