Tooling reliability is critical to welding success in friction stir welding, but tooling fatigue is not well understood because it occurs in conditions that are often unique to friction stir welding. A fatigue study was conducted on a commonly used tooling material, H13 tool steel, using constant stress loading at temperatures between 300°C and 600°C, and the results are presented. A model is proposed accounting for temperature and stress effects on fatigue life, utilizing a two-region Arrhenius temperature model. A transition in temperature effect on fatigue life is identified. Implications of the temperature effect for friction stir welding suggest that tooling fatigue life dramatically decreases above 500°C and accelerated testing should be conducted below 500°C.
| Identifer | oai:union.ndltd.org:BGMYU2/oai:scholarsarchive.byu.edu:etd-5441 |
| Date | 01 March 2015 |
| Creators | Jones, Bradley Valiant |
| Publisher | BYU ScholarsArchive |
| Source Sets | Brigham Young University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses and Dissertations |
| Rights | http://lib.byu.edu/about/copyright/ |
Page generated in 0.002 seconds