Complex bioactive fiber systems by means of electrospinning

Nanofibrous mats are interesting scaffold materials for biomedical applications like tissue engineering due to their interconnectivity and their size dimension which mimics the native cell environment. Electrospinning provides a simple route to access such fiber meshes. This thesis addresses the structural and functional control of electrospun fiber mats.
In the first section, it is shown that fiber meshes with bimodal size distribution could be obtained in a single-step process by electrospinning. A standard single syringe set-up was used to spin concentrated poly(ε-caprolactone) (PCL) and poly(lactic-co-glycolic acid) (PLGA) solutions in chloroform and meshes with bimodal-sized fiber distribution could be directly obtained by reducing the spinning rate at elevated humidity. Scanning electron microscopy (SEM) and mercury porosity of the meshes suggested a suitable pore size distribution for effective cell infiltration.
The bimodal fiber meshes together with unimodal fiber meshes were evaluated for cellular infiltration. While the micrometer fibers in the mixed meshes generate an open pore structure, the submicrometer fibers support cell adhesion and facilitate cell bridging on the large pores. This was revealed by initial cell penetration studies, showing superior ingrowth of epithelial cells into the bimodal meshes compared to a mesh composed of unimodal 1.5 μm fibers.
The bimodal fiber meshes together with electrospun nano- and microfiber meshes were further used for the inorganic/organic hybrid fabrication of PCL with calcium carbonate or calcium phosphate, two biorelevant minerals. Such composite structures are attractive for the potential improvement of properties such as stiffness or bioactivity. It was possible to encapsulate nano and mixed sized plasma-treated PCL meshes to areas > 1 mm2 with calcium carbonate using three different mineralization methods including the use of poly(acrylic acid). The additive seemed to be useful in stabilizing amorphous calcium carbonate to effectively fill the space between the electrospun fibers resulting in composite structures.
Micro-, nano- and mixed sized fiber meshes were successfully coated within hours by fiber directed crystallization of calcium phosphate using a ten-times concentrated simulated body fluid. It was shown that nanofibers accelerated the calcium phosphate crystallization, as compared to microfibers. In addition, crystallizations performed at static conditions led to hydroxyapatite formations whereas in dynamic conditions brushite coexisted.
In the second section, nanofiber functionalization strategies are investigated. First, a one-step process was introduced where a peptide-polymer-conjugate (PLLA-b-CGGRGDS) was co-spun with PLGA in such a way that the peptide is enriched on the surface. It was shown that by adding methanol to the chloroform/blend solution, a dramatic increase of the peptide concentration at the fiber surface could be achieved as determined by X-ray photoelectron spectroscopy (XPS). Peptide accessibility was demonstrated via a contact angle comparison of pure PLGA and RGD-functionalized fiber meshes. In addition, the electrostatic attraction between a RGD-functionalized fiber and a silica bead at pH ~ 4 confirmed the accessibility of the peptide.
The bioactivity of these RGD-functionalized fiber meshes was demonstrated using blends containing 18 wt% bioconjugate. These meshes promoted adhesion behavior of fibroblast compared to pure PLGA meshes.
In a second functionalization approach, a modular strategy was investigated. In a single step, reactive fiber meshes were fabricated and then functionalized with bioactive molecules. While the electrospinning of the pure reactive polymer poly(pentafluorophenyl methacrylate) (PPFPMA) was feasible, the inherent brittleness of PPFPMA required to spin a PCL blend. Blends and pure PPFPMA showed a two-step functionalization kinetics. An initial fast reaction of the pentafluorophenyl esters with aminoethanol as a model substance was followed by a slow conversion upon further hydrophilization. This was analysed by UV/Vis-spectroscopy of the pentaflurorophenol release upon nucleophilic substitution with the amines. The conversion was confirmed by increased hydrophilicity of the resulting meshes.
The PCL/PPFPMA fiber meshes were then used for functionalization with more complex molecules such as saccharides. Aminofunctionalized D-Mannose or D-Galactose was reacted with the active pentafluorophenyl esters as followed by UV/Vis spectroscopy and XPS. The functionality was shown to be bioactive using macrophage cell culture. The meshes functionalized with D-Mannose specifically stimulated the cytokine production of macrophages when lipopolysaccharides were added. This was in contrast to D-Galactose- or aminoethanol-functionalized and unfunctionalized PCL/PPFPMA fiber mats. / Biofunktionale Materialien gewinnen immer größere Bedeutung in biomedizinischen Anwendungen wie dem künstlichen Ersatz von Knochen oder Blutgefässe. Weiterhin können diese Stoffe nützlich sein, um die Wechselwirkung zwischen Biomaterialien und biologischen Systemen wie Zellen oder Organismen weiter zu erforschen. In diversen Studien konnten Größen wie dreidimensionaler Strukturaufbau, Oberflächentopographie, Mechanik und die Funktionalisierung mit bioaktiven Substanzen als Einflussfaktoren identifiziert werden, welche auf verschiedenen Größenskalen von makroskopisch bis nanoskopisch untersucht wurden und gegenwärtig erforscht werden. Bioinspiriert von Kollagenfasern, die als Strukturmotiv an verschieden Orten im menschlichen Körper vorkommen (z.B. extrazelluläre Matrix) konnte gezeigt werden, dass Fasermatten, die eine ähnliche Größendimensionen wie die vorher erwähnten Kollagenfasern (Ø ~ 500 nm) aufweisen, eine aussichtsreiche Gerüstmatrix darstellen. Eine einfache Methode Fasermatten in diesen Dimensionen herzustellen ist Elektrospinning, wobei typischerweise eine viskose Polymerlösung durch anlegen eines Hochspannungsfeldes verstreckt wird. Obwohl auf diese Weise hergestellte Fasermatten für gewisse Zelllinien eine ideale Zellwechselwirkung aufweisen, ist die Zellbesiedelung solcher Netzwerke, bedingt auch durch die kleinen Porendurchmesser, problematisch und bedarf meistens weiterer Prozessierungsschritte.
Diese Arbeit beschäftigt sich mit der einfachen Herstellung von strukturel und funktional kontrollierten Fasersystem mittels Elektrospinning. Der erste Teil behandelt ein Einschrittverfahren zum Elektrospinnen von bimodalen Fasermatten bestehend aus Nano- und Mikrofasern. In Zellstudien mit Epithelzellen konnte gezeigt werden, dass solche Netzwerke tiefer besiedelt werden als Matten bestehend aus unimodalen 1.5 μm dicken Fasern. Des Weiteren wurden diese Fasermatten für fasergerichtete Kristallisation von Kalziumcarbonat und – phosphat benutzt.
In einem zweiten Teil wurden 2 Strategien für die Faserfunktionalisierung mit Peptiden und Zuckermolekülen entwickelt. Zum einen wurde gezeigt, dass funktionale Peptidfasern durch Verspinnung einer Mischung von einem Peptid-Polymer-Konjugat mit einem kommerziellen Polymer hergestellt werden konnten. Zusätzlich wurde ein modularer Ansatz für die Herstellung von reaktiven Fasern ausgearbeitet, die anschließend mit Peptiden oder Zuckern funktionalisiert wurden. Die Bioaktivität der Zucker funktionalisierten Fasern konnte durch Zellversuche erfolgreich bestätigt werden.

Identiferoai:union.ndltd.org:Potsdam/oai:kobv.de-opus-ubp:4490
Date January 2010
CreatorsGentsch, Rafael
PublisherUniversität Potsdam, Mathematisch-Naturwissenschaftliche Fakultät. Institut für Chemie
Source SetsPotsdam University
LanguageEnglish
Detected LanguageEnglish
TypeText.Thesis.Doctoral
Formatapplication/pdf
Rightshttp://opus.kobv.de/ubp/doku/urheberrecht.php

Page generated in 0.0025 seconds