The aim of this thesis was to analyze the formation of defects in a given casting of ductile cast iron EN - GJS - 600-3 cast in sand molds bentonite, which is formed jolting with coining and then find a solution to remedy these defects. To resolve this issue, the influence of the composition of the sand mixture, the effect of metal flow in a cavity forms and the influence of deoxidation of metal in the presence of defects. Obtained results showed the importance of the influence Reoxidation metal cavity mold. Specifically, in this case succeeded in reducing the incidence of PINHOLES. Removal of PINHOLES to achieve deoxidation aluminum melt. This has reduced the production of nonconforming castings under 3% from the original 6.5%.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:229125 |
| Date | January 2010 |
| Creators | Opačitý, Radim |
| Contributors | Palán, Petr, Šenberger, Jaroslav |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0013 seconds