Previous issue date: 2015 / Entre as membranas inorgânicas microporosas, as membranas zeolíticas constituem
uma tecnologia promissora, devido às suas potenciais aplicações normalmente
na desidratação do álcool, separação de moléculas de gás, separação de isômeros
ou em processos químicos, incluindo reações de esterificação. Sob este aspecto,
torna-se imprescindível o estudo das rotas de preparação desses materiais, visando
desenvolver produtos com qualidade e a baixo custo. Portanto, a inovação deste
estudo se dá na síntese de membranas zeolíticas via método de síntese poreplugging
visando a utilização das membranas inorgânicas para permeação gasosa
de N2. Neste trabalho foram desenvolvidos os seguintes materiais: zeólita ZSM-5,
membranas cerâmicas (γ-alumina e α-alumina) e as membranas zeolíticas (ZSM5/γ-alumina e ZSM-5/α-alumina). A zeólita ZSM-5 foi sintetizada por meio do método
hidrotérmico. As membranas cerâmicas (γ-alumina e α-alumina) foram preparadas a
partir da técnica de conformação de pós cerâmicos e posteriormente submetidas à sinterização a uma temperatura de 1000 ºC/1h e 1200 ºC/1h respectivamente. A
preparação das membranas zeolíticas (ZSM-5/γ-alumina e ZSM-5/α-alumina) foi
realizada com base no método pore in plugging. As amostras foram caracterizadas a
partir das técnicas de difração de raios X e Microscopia Eletrônica de Varredura. Os
resultados experimentais permitem diversas conclusões acerca do desenvolvimento
dos materiais: zeólita ZSM-5, membranas cerâmicas (γ-alumina e α-alumina) e
membranas zeolíticas (ZSM-5/γ-alumina e ZSM-5/α-alumina). A partir da difração de
raios X, foi possível verificar que o método de síntese empregado, foi efetivo na
obtenção da zeólita ZSM-5. O difratograma apresentou picos característicos de uma
zeólita ZSM-5 quando comparada ao padrão. Os resultados obtidos por DRX para
as membranas cerâmicas (γ-alumina e α-alumina) demonstraram a formação de
picos característicos do óxido de alumínio, os materiais são cristalinos e puros. Para
o método pore-plugging pode se dizer que é um método promissor, pois mostrou
uma formação satisfatória da camada zeolítica no resultado do DRX de ambas as
membranas zeolíticas (ZSM-5/γ-alumina e ZSM-5/α-alumina). / Among the microporous inorganic membranes, zeolite membranes are a promising
technology due to their potential applications normally in alcohol dehydration,
separation of gas molecules, separation of isomers or chemical processes, including
esterification reactions. In this regard, it is essential to study the preparation of these
materials routes in order to develop products with quality and low cost. Therefore,
innovation of this study gives the synthesis of zeolite membranes via pore-plugging
synthesis method aimed at the use of inorganic membranes for gas permeation N2.
In this work the following materials were developed: ZSM-5 zeolite, ceramic
membranes (γ-alumina and α-alumina) and zeolitic membranes (ZSM-5/γ-alumina
and ZSM-5/α-alumina). Zeolite ZSM-5 was synthesized by the hydrothermal method.
Ceramic membranes (γ-alumina and α-alumina) were prepared from the ceramic
powder forming technique, and subsequently subjected to a sintering temperature of
1000 °C/1h and 1200 °C/1h respectively. The preparation of zeolite membranes
(ZSM-5/γ-alumina and ZSM-5/α-alumina) was carried out based on the method in
pore plugging. The samples were characterized from the techniques of X diffraction
and scanning electron microscopy rays. The experimental results allow several
conclusions about the development of materials: zeolite ZSM-5, ceramic membranes
(γ-alumina and α-alumina) and zeolite membranes (ZSM-5/γ-alumina and ZSM-5/αalumina).
From the X-ray diffraction, it found that the method of synthesis used was
effective in obtaining the zeolite ZSM-5. The XRD pattern showed peaks
characteristic of ZSM-5 compared to the standard. The results obtained by XRD
ceramic membranes (γ-alumina and α-alumina) showed the formation of peaks
characteristic of aluminum oxide, the materials are crystalline and pure. For the poreplugging
method can be said to be a promising method because it showed a
satisfactory formation of the zeolite layer on the result of XRD both zeolite
membranes (ZSM-5/γ-alumina and ZSM-5/α-alumina).
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/315 |
| Date | 23 March 2018 |
| Creators | SCHEIBLER, Janaina Rafaella. |
| Contributors | RODRIGUES, Meiry Gláucia Freire., SILVA, Maristela Alves da., VASCONCELOS, Luis Gonzaga Sales. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Petrobras e ANP/PRH-25 |
Page generated in 0.0021 seconds