Efeito da incorporação do trimetafosfato de sódio microparticulado e nanoparticulado ao cimento de ionômero de vidro nas propriedades físico-mecânicas e na desmineralização do esmalte

Made available in DSpace on 2016-02-05T18:30:10Z (GMT). No. of bitstreams: 0
Previous issue date: 2015-08-28. Added 1 bitstream(s) on 2016-02-05T18:34:20Z : No. of bitstreams: 1
000857869.pdf: 2789826 bytes, checksum: cecfa33b798ebbee35330f861246deea (MD5) / O objetivo do presente estudo foi avaliar o efeito da incorporação do trimetafosfato de sódio (TMP) microparticulado (m) e nanoparticulado (n) ao cimento de ionômero de vidro (CIV) nas propriedades físico-mecânicas e na desmineralização do esmalte. Foram confeccionados corpos-de-prova (n=54) para cada grupo experimental: CIV sem TMP (CIV), CIV com TMPm 3,5%, 7% e 14% e CIV com TMPn 3,5%, 7% e 14%. Seis corposde- prova foram utilizados na determinação da liberação de fluoreto (F) e TMP em soluções de desmineralização e de remineralização durante 15 dias. As propriedades físico-mecânicas avaliadas 24 horas e 7 dias após a confecção foram: resistência à compressão (n=12), resistência à tração diametral (n=12), dureza de superfície do material (n=6) e grau de conversão de monômeros (n=6). Para o estudo da desmineralização do esmalte, corpos-de-prova (n=12) foram adaptados a blocos de esmalte selecionados pelo teste de dureza de superfície inicial (DS1) e submetidos às ciclagens de pH. A seguir, determinou-se a dureza de superfície final (DS2), em secção longitudinal (DSL) e a concentração de F no esmalte. Testes paramétricos e não paramétricos foram realizados, após a verificação da homocedasticidade dos dados (p<0,05). A adição de 14% de TMP levou a maior média de liberação de F (p<0,05) e os demais grupos foram similares ao CIV (p>0,05). Maior liberação de TMP foi observada com 14% microparticulado (p<0,05). A incorporação do TMP ao CIV promoveu uma redução média nas propriedades mecânicas de 21% (tração), 10% (compressão) e 18% (dureza), após 24 horas e em 18%, 23% e 12%, após 7 dias. O grau de conversão foi menor com adição de 14% TMP quando comparado ao CIV após 24 horas (p<0,05); no tempo de 7 dias não houve diferença entre os grupos (p>0,05). A adição de 7% e 14% de... / The aim of this study was to evaluate the effect of addition of sodium trimetaphosphate (TMP) microparticle (m) and nanoparticle (n) to the glass ionomer cement (GIC) on the physico-mechanical properties and demineralization of the enamel. Specimens (n=54) were fabricated from each experimental group: GIC without TMP (GIC), GIC with 3.5%, 7% and 14% TMPm and GIC with 3.5%, 7% and 14% TMPn. To determine the release of fluoride (F) and TMP it was used six specimens immersed into a demineralization and remineralization solution during 15 days. The physico-mechanical properties evaluated 24 hours and 7 days after fabrication were: compressive strength (n=12), diametral tensile strength (n=12), surface hardness of material (n=6) and the degree of conversion of monomers (n=6). For the study of enamel demineralization, specimens (n=12) were attached to enamel blocks selected by the initial surface hardness test (SH1) and submitted to the pH-cycling. Following, final surface (SH2) and cross-sectional (CSH) hardness, as well as enamel F concentration were determined. Parametric and non-parametric tests were performed after checking the data homoscedasticity (p<0.05). The addition of 14% TMP led to higher mean release of F (p<0.05) and the other groups were similar to the GIC (p>0.05). The release of TMP was higher with 14% microparticulate (p<0.05). The addition of TMP at GIC promoted an average reduction of mechanical properties of 21% (tensile), 10% (compressive) and 18% (hardness) after 24 hours and 18%, 23% and 12% after 7 days. The degree of conversion was lower with addition of 14% TMP compared to the GIC after 24 hours (p<0.05); at 7 days there was no difference between groups (p>0.05). Addition of 7% and 14% TMP reduced mineral loss and increased enamel F concentration when compared...

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/134202
Date28 August 2015
CreatorsAbreu, Valéria Marisel de [UNESP]
ContributorsUniversidade Estadual Paulista (UNESP), Ostini, Denise Pedrini [UNESP], Delbem, Alberto Carlos Botazzo [UNESP]
PublisherUniversidade Estadual Paulista (UNESP)
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format68 f : il. + 1 CD-ROM
SourceAleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP
Rightsinfo:eu-repo/semantics/openAccess
Relation-1, -1, -1

Page generated in 0.0029 seconds