Previous issue date: 2012-01-01 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Avaliou-se a liberação de íon fluoreto de 2 cimentos de ionômero de vidro (CIV) anidro e 2 CIVs modificados por resina composta antes e após recarga com fluoreto de sódio neutro a 2% por 4min. e a proteção da superfície do CIV Maxxion R com um adesivo odontológico, um verniz cavitário e um esmalte incolor para unhas. Com uma matriz de aço inox com 2mm x 6mm, confeccionou-se 5 corpos de prova de cada material, os quais foram imersos em 5mL de água deionizada, trocada a cada 24h. Foram realizadas leituras em um potenciômetro calibrado acoplado a um eletrodo sensível a íons fluoreto nos dias 1, 2, 9 e 17 na 1ª e 2ª etapas, e as amostras foram tamponadas com solução TISAB III. Na 2ª etapa, as amostras foram submetidas à recarga e em seguida lavadas, secas e novamente imersas em 5mL de água deionizada. Na 3ª etapa foi realizada a proteção da superfície dos CIVs e feitas leituras nos 5min., 24h, 48h e 72h. Os dados foram submetidos aos testes estatísticos Post Hoc de Tukey e t Student (p<0,05). Concluiu-se que os CIVs anidros tiveram maior efetividade na liberação de íon fluoreto em comparação com os CIVs modificados por resina composta e o Maxxion R apresentou um comportamento homogêneo e estatisticamente significante nas duas etapas. Os CIVs possuem a capacidade de recarregar, especialmente os anidros. Todos os materiais protetores testados foram eficazes, e o esmalte incolor para unhas apresentou o melhor comportamento. / Was evaluated the fluoride ion release of 2 glass ionomer cements (GIC) and anhydrous 2 resin-modified GICs made before and after charge neutral sodium fluoride to 2% for 4 minutes. and protecting the surface of the IVC Maxxion R with a dental adhesive, a cavity varnish and a colorless nail polish. With an array of stainless steel with 6mm x 2mm, it was made five specimens of each material, which were immersed in 5 mL of deionized water, changed every 24 hours. Readings were taken in a calibrated potentiometer coupled to an electrode sensitive to fluoride ions on days 1, 2, 9 and 17 in the 1st and 2nd stages, and the samples were buffered with TISAB III solution. In Step 2, the samples were submitted to recharge and then washed, dried and again immersed in 5 mL of deionized water. In Step 3 was done to protect the surface of GICs and readings made in 5min., 24h, 48h and 72h. The data were subjected to statistical tests post hoc Tukey et Student (p <0.05). It was concluded that the GICs were more effective in anhydrous fluoride ion release compared to composite resin modified GICs and Maxxion R had a homogeneous behavior and statistically significant in two steps. The GICs have the ability to recharge, especially anhydrous. All protective materials tested were effective, and nail incolor enamel showed the best behavior.
| Identifer | oai:union.ndltd.org:IBICT/oai:hermes.cpd.ufjf.br:ufjf/4552 |
| Date | 01 January 2012 |
| Creators | Antunes, Débora Pinto |
| Contributors | Salgado, Ivone de Oliveira, Matos, Renato Camargo, Costa, Leonardo César, Pazinatto, Rafael Barroso |
| Publisher | Universidade Federal de Juiz de Fora (UFJF), Programa de Pós-graduação em Clínica Odontológica, UFJF, Brasil, Faculdade de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFJF, instname:Universidade Federal de Juiz de Fora, instacron:UFJF |
| Rights | info:eu-repo/semantics/openAccess |