The role of the oxide/organic and organic/organic interfaces in small-molecule planar-Heterojunction (PHJ) photovoltaics was investigated with three interrelated projects: i) indium-tin oxide (ITO) bottom contact electrodes were modified with gold nanoparticles (Au-NPs) to improve rates of charge-transfer at the donor/oxide interface, ii) donor layers in OPVs were textured to increase charge generation at the organic/organic' interface, and iii) the effect of co-facial overlap on device performance via tuning of the electron acceptor orientation at the organic/organic interface. The modification of ITO with Au-NPs showed increased performance in small-molecule OPVs when compared to non-processed ITO devices due to the interactions between the Au-NPs and the donor material. Textured TiOPc increased overall device performance by a factor of 2X via the increased surface area, near-IR absorption, and increased mobilities. Modified and un-modified PTCDA acceptors showed that co-facial overlap at the organic/organic' interface is a large determinant in device performance, while the performance in small-molecule planar-heterojunction photovoltaics were severely affected by the pre-treatment process, most likely due to the particular interactions between the oxide and the donor material.
| Identifer | oai:union.ndltd.org:arizona.edu/oai:arizona.openrepository.com:10150/202936 |
| Date | January 2011 |
| Creators | Placencia, Diogenes |
| Contributors | Armstrong, Neal R., Pemberton, Jeanne, Monti, Oliver L., Loy, Douglas A., Saavedra, S. Scott, Armstrong, Neal R. |
| Publisher | The University of Arizona. |
| Source Sets | University of Arizona |
| Language | English |
| Detected Language | English |
| Type | text, Electronic Dissertation |
| Rights | Copyright © is held by the author. Digital access to this material is made possible by the University Libraries, University of Arizona. Further transmission, reproduction or presentation (such as public display or performance) of protected items is prohibited except with permission of the author. |
Page generated in 0.0019 seconds