O presente trabalho estudou os efeitos das intera»c~oes hiper¯nas em dois sistemas de ¶oxidos: RCoO3 (R = Gd e Tb) com estrutura perovskita e ¯lmes ¯nos monocristalinos de HfO2 por meio da t¶ecnica de Correla»c~ao Angular Gama-Gama Perturbada (CAP), com o objetivo de fazer um estudo sistem¶atico do comportamento da varia»c~ao do gradiente de campo el¶etrico em fun»c~ao da temperatura. Para realiza»c~ao das medidas de intera»c~oes de quadrupolo el¶etrico utilizamos como de pontas de prova os n¶ucleos 111In ¡!111 Cd e o 181Hf ¡!181 Ta. As amostras de perovskitas foram confeccionadas por meio de um processo qu¶³mico denominado Sol-Gel e as an¶alises foram realizadas com aux¶³lio de difra»c~ao de raios-X. As pontas de prova foram inseridas nas solu»c~oes qu¶³micas durante o preparo das amostras. Os ¯lmes ¯nos foram fornecidos pelo Laborat¶orio de Intera»c~oes Hiper¯nas da Universidade de Lisboa e a ponta de prova de 181Hf foi ativada por meio da irradia»c~ao do ¯lme ¯no no reator IEA-R1 do IPEN no tempo adequado a espessura do ¯lme. As medidas foram realizadas na faixa de temperatura de 10 - 1560 K. Os resultados das medidas das amostras de perovskita indicam uma depend^encia do GCE com o s¶³tio de ocupa»c~ao dos ¶atomos da ponta de prova e uma varia»c~ao do GCE com a temperatura, que pode ser explicada por transi»c~oes de spins no ¶atomo de Co. As medidas do GCE dos ¯lmes ¯nos com mesma espessura apresentam uma segunda fra»c~ao, al¶em daquela correspondente a freqÄu^encia da HfO2 em amostras de bulk. / In the present work, the Perturbed Angular Gamma-Gamma Correlation technique (PAC) was used to measure the Electric Field Gradient (EFG) in two oxide systems: RCoO3 (R = Gd, Tb) perovskite oxide and HfO2 in order to study the behavior of the EFG as a function of temperature. Electric quadrupole hyper¯ne interaction measure- ments were carried out using 111In ¡!111 Cd and 181Hf ¡!181 Ta radioactive probe nuclei. The samples were prepared through a chemical route known as Sol-Gel technique and analyzed with x-ray di®raction. Both nuclei were introduced in to the perovskite samples during the chemical procedure. The thin ¯lms were provided by the Laboratory of Hyper¯ne Interactions at the University of 181Hf Lisbon and the probe nuclei was activated by the irradiation of the thin ¯lm in the reactor of IPEN IEA-R1 at an appropriate time regarding the thickness of the ¯lm. The measurements were taken in the temperature range from 4 K to 1560 K. The results for the perovskite oxides measurements show a site-dependence of the EFG with probe-nuclei occupation and a temperature dependence of EFG that can be explained if spins transitions in Co are considered. The results of EFG measurements in the 25 nm thin ¯lm of HfO2 show a second fraction besides that corresponding to bulk.
Identifer | oai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-05102009-143114 |
Date | 10 March 2009 |
Creators | Cavalcante, Fabio Henrique de Moraes |
Contributors | Carbonari, Artur Wilson |
Publisher | Biblioteca Digitais de Teses e Dissertações da USP |
Source Sets | Universidade de São Paulo |
Language | Portuguese |
Detected Language | English |
Type | Tese de Doutorado |
Format | application/pdf |
Rights | Liberar o conteúdo para acesso público. |
Page generated in 0.2668 seconds