The effects of octadecylamine-functionalized reduced graphene oxide (FRGO) on the frictional and wear properties of diglycidylether of bisphenol-A (DGEBA) epoxy are studied using a pin-on-disk tribometer. It was observed that the addition of FRGO significantly improves the tribological, mechanical, and thermal properties of epoxy matrix. Graphene oxide (GO) was functionalized with octadecylamine (ODA), and then reduction of oxygen-containing functional groups was carried out using hydrazine monohydrate. The Raman and x-ray photoelectron spectroscopy studies confirm significant reduction in oxygen-containing functional groups and formation of ODA functionalized reduced GO. The nanocomposites are prepared by adding 0.1, 0.2, 0.5 and 1.0 wt % of FRGO to the epoxy. The addition of FRGO increases by more than an order of magnitude the sliding distance during which the dynamic friction is ≤ 0.1. After this distance, the friction sharply increases to the range of 0.4 - 0.5. We explain the increase in sliding distance during which the friction is low by formation of a transfer film from the nanocomposite to the counterface. The wear rates in the low and high friction regimes are approximately 1.5 x 10-4 mm3/N·m and 5.5 x 10-4 mm3/N·m, respectively. The nanocomposites exhibit a 74 % increase in Young’s modulus with 0.5 wt. % of FRGO, and an increase in glass transition and thermal degradation temperatures.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc699889 |
| Date | 08 1900 |
| Creators | Shah, Rakesh K. |
| Contributors | Perez, Jose, Weathers, Duncan L., Philipose, Usha, Verbeck, Guido F. |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | xi, 83 pages : illustrations (some color), Text |
| Rights | Public, Shah, Rakesh K., Copyright, Copyright is held by the author, unless otherwise noted. All rights reserved. |
Page generated in 0.0021 seconds