Investigation of the microstructure of nuclear grade matrix graphite

This dissertation focuses on the investigation of the microstructures of two nuclear grade matrix graphites. These graphites were intended for use in the core components of a high temperature test reactor (HTTR) of the pebble bed modular reactor (PBMR) design. The graphites were provided in the form of fuel spheres and a reflector block. The techniques used in the analysis of the materials include fracturing, etching, scanning electron microscopy (SEM), nano-indentation, x-ray diffraction (XRD) and transmission electron microscopy (TEM). The microstructures of the materials were characterized successfully. The fuel sphere material consisted of a high concentration of curved graphite flakes and grains in contact with turbostratic matrix graphite. The well graphitized flakes and grains were polycrystalline in nature. Delamination cracks were prevalent in the graphite crystallites. There was no significant difference in the microstructures of the center, interior and surface regions of the fuel sphere material. No evidence of amorphous carbon or resin residues was found. The reflector material consisted of a low concentration of graphite crystallites embedded within turbostratic matrix graphite. Delamination cracks were observed within the graphite crystallites, and many cavities were present in the material. TEM observation also revealed the presence of diamond crystallites. It was concluded that the fuel sphere graphite was most probably suitable for use as is, provided that the material also possessed other required properties for use in a HTTR. The reflector material however was considered to be unsuitable for use in a HTTR. It was thus suggested that the reflector material could be made more suitable by sufficient graphitization of the turbostratic graphite which formed the bulk of the material.

Identiferoai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:nmmu/vital:10540
Date January 2009
CreatorsDowney, Justin Michael
PublisherNelson Mandela Metropolitan University, Faculty of Science
Source SetsSouth African National ETD Portal
LanguageEnglish
Detected LanguageEnglish
TypeThesis, Masters, MSc
Formatx, 154 leaves, pdf
RightsNelson Mandela Metropolitan University

Page generated in 0.0015 seconds