NanopartÃculas magnÃticas de NiFe2O4 foram sintetizadas pelo mÃtodo sol-gel protÃico, a partir de uma soluÃÃo aquosa contendo gelatina comestÃvel (GelitaTM) e sais de nÃquel(II) e ferro(III), apÃs a secagem uma resina foi formada e em seguida foi analisada por Termogravimetria e OxidaÃÃo à Temperatura Programada (OTP). As amostras de NiFe2O4 foram obtidas pela calcinaÃÃo das resinas durante 4 horas em vÃrias temperaturas (250oC, 300oC, 400oC, 600oC, 800oC e 1000oC) e em 400oC com variaÃÃo de tempo (2h, 3h e 4h). O pà resultante foi caracterizado por espectroscopia de infravermelho, difraÃÃo de raios X, microscopia eletrÃnica de transmissÃo (MET), microscopia eletrÃnica de varredura (MEV) e espectroscopia de energia dispersiva (EDS). As propriedades magnÃticas das amostras foram investigadas por espectroscopia MÃssbauer e Medidas MagnÃticas, a temperatura ambiente; as medidas magnÃticas foram feitas em um magnetÃmetro de amostra vibrante (VSM). Os parÃmetros estruturais extraÃdos da difraÃÃo de raios X foram refinados pelo mÃtodo Rietveld; o tamanho mÃdio dos cristalitos foi determinado pela equaÃÃo de Scherrer e pelo mÃtodo grÃfico de Williamson-Hall, a partir dos valores da largura a meia altura dos picos de difraÃÃo (FWHM â Full Width at Half Maximum); pelo mÃtodo grÃfico de Williamson-Hall foi determinada a microdeformaÃÃo. O tamanho mÃdio de cristalito variou de 4,9nm atà 69,5nm e menores microdeformaÃÃes reduziram a diferenÃa de tamanho calculados pela equaÃÃo de Scherrer e pelo grÃfico de Williamson-Hall. A fim de indicar uma possÃvel aplicaÃÃo para as nanopartÃculas de NiFe2O4 foram realizados testes de toxicidade in vivo. / Magnetic nanoparticles of NiFe2O4 were synthesized by the proteic sol-gel method,using nickel (II) and iron (III) nitrates and aqueous solution of gelatin (GelitaTM). The
dried solution in the form of resin, were characterized by thermogravimetric analysis(TGA), combined with the temperature-programmed oxidation (TPO). The sampleso o o oof NiFe2O4 were synthesized at different temperatures (250 C, 300 C, 400 C, 600 C,800o C e 1000oC), the annealing time interval was of 4 h; and 400oC for differentsintering times (2h, 3h e 4h). The obtained nanoparticles werecharacterized byinfrared spectroscopy, X-ray powder diffraction (XRD), transmission electronmicroscopy (TEM), scanning electron microscopy (SEM), energy dispersivespectrometer (EDS). Magnetic properties were investigated by spectroscopy
MÃssbauer and Magnetization measurements obtained at room temperature;magnetization measurements was used a vibrating sample magnetometer (VSM).The microstructural parameters from the X-ray powder diffraction have beendetermined by means of Rietveld analysis; nanoparticle sizes calculated by theScherrer equation and size-strain by Williamson-Hall (W-H) method, using the FullWidth at Half Maximum (FWHM) of the diffraction peaks. The average particlediameter ranges from 4,9nm to 69,5nm. Toxicity tests were performed in vivo todetermine application for NiFe2O4.
Identifer | oai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:7485 |
Date | 29 November 2013 |
Creators | NÃbia Alves de Souza Nogueira |
Contributors | Jose Marcos Sasaki, Ricardo EmÃlio Ferreira Quevedo Nogueira, Antoninho Valentini, Mauro Luciano Baesso, JoÃo Maria Soares |
Publisher | Universidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em Engenharia e CiÃncia de Materiais, UFC, BR |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | application/pdf |
Source | reponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0351 seconds