The NaCaAlF₆-Al₂O₃ and Na₃AlF₆-Al₂O₃-NaCaAlF₆ phase diagrams were determined using DTA, x-ray diffraction, quench analysis, and optical microscopy. The NaCaAlF₆-Al₂O₃ system was a simple eutectic system with the eutectic located below 0.5 weight percent NaCaAlF₆. The ternary system was a eutectic system showing solid solution of NaCaAlF₆ in both polymorphs of Na₃AlF₆. Alumina exhibited no appreciable solubility in Na₃AlF₆ and, in the ternary system, less than 2% solubility above 15% NaCaAlF₆. / Master of Science
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/87140 |
| Date | January 1982 |
| Creators | Parks, William P. |
| Contributors | Materials Engineering |
| Publisher | Virginia Polytechnic Institute and State University |
| Source Sets | Virginia Tech Theses and Dissertation |
| Language | en_US |
| Detected Language | English |
| Type | Thesis, Text |
| Format | vi, 74 leaves, application/pdf, application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
| Relation | OCLC# 9403382 |
Page generated in 0.0022 seconds