Orientadores: Lourenço Correr Sobrinho, Carlos Jose Soares / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-19T04:51:56Z (GMT). No. of bitstreams: 1
Naves_LucasZago_D.pdf: 3401396 bytes, checksum: 30dc89e0c7e18900c68d45a72ce79505 (MD5)
Previous issue date: 2011 / Resumo: O objetivo neste estudo foi avaliar as propriedades mecânicas, ópticas e de superfície da cerâmica termo-prensada IPS Empress Esthetic (Ivoclar Vivadent, Schan, Liechestein). Discos cerâmicos (12 mm x 0,9 mm) foram termo-prensados em forno específico do sistema (EP 500, Ivoclar Vivadent) e serviram como controle (TP1). Remanescentes (sprues e botões cerâmicos) do grupo controle foram reaproveitados e utilizados para a confecção de espécimes dos grupos de re-prensados (processados 2 vezes -TP2 e processados 3 vezes - TP3). Todos os processos de termo-prensagem foram realizados de acordo com as instruções dos fabricantes. A dureza Vickers (VHN) foi mensurada em durômetro HMV 2 (Shimadzu), com carga de 0,5 kgf aplicada por 10 segundos. Cinco medidas foram feitas para cada amostra (n = 5). A resistência à flexão biaxial (BFS) (ISO 6872) foi realizada para determinar a resistência dos discos prensados e re-prensados (n = 10), com velocidade de aplicação de carga de 0,5 mm/min., em máquina de ensaios mecânicos (4411; Instron Inc., Canton, MA, USA). Irradiância e características do espectro luminoso transmitido através da cerâmica (em três espessuras para cada termo-prensagem: 0,7; 1,4 e 2 mm) foram mensurados por meio de potenciômetro e espectrômetro digitais. Características de superfície foram avaliadas em microscopia eletrônica de varredura (MEV), em modo elétron secundário (SEI). Análise das micrografias foram realizadas no programa de pós-processamento de imagens ImageJ (NIH, Londres, Reino Unido), objetivando verificar a concentração cristalina da leucita e características de superfície em imagens 3D (plotagem de superfície). Os dados foram analisados estatisticamente (ANOVA + Tukey post hoc HSD, P <0,05). Os valores obtidos de dureza foram (em VHN) TP1: 589,1 ± 18,1; TP2: 551,8 ± 13,9; TP3: 552 ± 22,2 . Os grupos re-prensados (TP2, TP3) apresentaram média de dureza estatisticamente menor que o grupo controle (TP1). Os dados obtidos da resistência a flexão biaxial foram (em MPa) TP1: 219,70 ± 17,92; TP2: 180,66 ± 38,73; TP3: 171,85 ± 32,56. O grupo controle (TP1) apresentou média estatisticamente superior aos grupos re-prensados (TP2 e TP3). As micrografias mostraram aumento no tamanho e concentração de cristais de leucita, para os grupos experimentais. A análise das imagens mostrou diminuição da homogeneidade na distribuição dos cristais de leucita na fase vítrea e aumento na densidade cristalina após repetidas termo-prensagens. Redução da irradiância através dos corpos-de-prova foi detectada com o aumento da espessura da cerâmica, e alteração do perfil de emissão foi observada após repetidas termo-prensagens. O reaproveitamento do material cerâmico IPS Empress Esthetic alterou propriedades mecânicas e propriedades ópticas interferindo na passagem de luz através do corpo cerâmico. Sucessivas termo-prensagens alteraram também a microestrutura da cerâmica vítrea reforçada por leucita IPS Empress Esthetic / Abstract: The aim of this study was to evaluate the mechanical, optical and surface properties of one heat-pressed glass-ceramic material after repeated heat-pressing. One commercially available heat-pressed glass-ceramic system IPS Empress Esthetic was selected. Disc samples (12 mm x 0.9 mm) of each tested material were heat-pressed and used as control (TP1). Sprue and button parts of the pressed groups were retrieved and used for repeated heat-pressing to construct specimens of re-pressed groups (TP2 and TP3). All the heat-pressed casting procedures were performed according to the manufacturers' instructions. The Vickers hardness number (VHN) was measured with HMV 2 microhardness tester (Shimadzu), with a load of 0.5 Kgf applied for 10 seconds. Five measurements were made for each specimen (n=5). A biaxial flexural strength (BFS) test (ISO 6872) was performed to determine the strength of pressed and re-pressed glass-ceramic disc specimens (n = 10) at a crosshead speed of 0.5 mm/min. Light irradiance and spectrum characteristics transmitted through ceramic were measured using a power meter and a light spectrometer. Surface characteristics were examined with secondary electron imaging (SEI) in SEM. Post-processing image analysis were made in ImageJ (NIH, London, UK) software to access leucite crystalline density and plot surface characteristics in 3D images. The data were analysed statistically (ANOVA + Tukey's HSD post hoc test, P < 0.05). The VHN values obtained was TP1: 589.1 ± 18.1; TP2: 551.8 ± 13.9; TP3: 552 ± 22.2. The re-pressed groups (TP2, TP3) had a statistically significant lower VHN mean than the pressed control group (TP1). The BFS (MPa) values obtained was TP1:219.70 ± 17.92; TP2:180.66 ± 38.73; TP3: 171.85 ± 32.56. The pressed group (TP1) group had a statistically significant higher BFS mean than the re-pressed groups (TP2 and TP3). The SEM micrographs of the leucite-reinforced glass-ceramic material showed an increase in size and concentration of leucite crystals after repeated heat-pressing, post-processing imaging analysis showed inhomogeneity of leucite crystals distribution and increase in crystal density after repeated heat-pressing. A decrease in irradiance was detected with increasing ceramic thickness, and alteration in the emission profile was observed after repeated heat-pressing. Repeated heat-pressing treatment produced a statistically significant decresase in the mechanical properties and suggests alterations in optical properties in the evaluated IPS Empress Esthetic glass-ceramic material. Microstructural alterations was also detected / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289597 |
| Date | 19 August 2018 |
| Creators | Naves, Lucas Zago, 1981- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Soares, Carlos José, Correr Sobrinho, Lourenço, 1960-, Neto, Alfredo Julio Fernandes, Neves, Flávio Domingues das, Sinhoreti, Mário Alexandre Coelho, Consani, Simonides |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 67 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |