Previous issue date: 2007-02-28 / A sílica hexagonal mesoporosa modificada com ácido carboxílico (SiAc) foi obtida pela síntese de um novo agente sililante produzido a partir da reação entre o ácido cloro-acético e 3-aminoproprilmetoxissilano, o qual foi imobilizado na sílica pelo processo sol-gel direcionado por n-dodecilamina. A SiAc foi 29 13 caracterizada por TG, FTIR, Si-RMN, C-RMN, MEV, densidade superficial de carga, área superficial e diâmetro de poros, que comprovaram que o grupo carboxílico estava covalentemente ligado a matriz inorgânica e que o material apresenta uma estrutura nanométrica com esferas < 50 nm e com poros de 10 nm. Os herbicidas 2,4-D, diuron e picloram foram ancorados nos poros da SiAc, formando os materiais SiD, SiDi e SiPi, respectivamente. A liberação do picloram da matriz de sílica foi mais lenta em comparação com a liberação das -5 -1 matrizes contendo diuron e 2,4-D. Em 26 dias de liberação, 4,43•10 mol L de -5 -5 -1 picloram foram liberados pela sílica SiPi, enquanto 5,0•10 e 1,4•10 mol L foram liberadas pelas amostras SiD e SiDi, em 30 e 20 dias, respectivamente.
_________________________________________________________________________________________ ABSTRACT / Hexagonal mesoporous sílica modified with carboxylic acid (SiAc) has been obtained by reaction between chloroacetic acid and 3- aminopropyltrimetoxysilane, which was immobilized in silica porous by sol-gel process in presence of n-dodecylamine template. SiAc was characterized by 29 13 TG, FT-IR, Si-NMR, C-NMR, SEM, surface charge density, surface area and porous diameter, which proved that carboxylic group was chemically bonded to inorganic structure, and the material presented nanometric structure with spheres < 50 nm and porous with 10 nm. Herbicides 2,4-D, diuron and picloram was anchored in SiAc porous gel to produce the materials named SiD, SiDi and was slower SiPi, respectively. The controlled release of picloram from the SiAc -5 -1 than diuron and 2,4-D. After 26 days of releasing, 4.43•10 mol L of picloram -5 -5 -1 were delivered by SiPi, 5.0•10 and 1.4•10 mol L were released from the SiD and SiDi, in 30 and 20 days, respectively.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/3168 |
| Date | 28 February 2007 |
| Creators | Torres, Jocilene Dantas |
| Contributors | Prado, Alexandre Gustavo Soares do |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds