Orientador: Roseana da Exaltação Trevisan / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-15T00:22:28Z (GMT). No. of bitstreams: 1
PereaCorimaya_RodrigoLuis_M.pdf: 2032359 bytes, checksum: 4a5d338de38fffae7ef6f96cce297aaa (MD5)
Previous issue date: 2009 / Resumo: No desenvolvimento deste trabalho utilizou-se o ensaio de auto-restrição TEKKEN com o propósito de adequar este teste para a avaliação do trincamento da junta soldada do aço API X80. Para a execução das soldas foi usado o processo de soldagem a arco com eletrodo tubular (FCAW), utilizando o aço API X80 e os eletrodos E71T-1 e E 71T8-K6. O desenvolvimento experimental realizou-se através do planejamento fatorial 23 (PF); as variáveis de influência estudadas foram: a temperatura de preaquecimento, o tipo de arame tubular e o tipo de chanfro do teste. Como variável de resposta foi avaliada a presença de trincas na junta soldada. Os resultados obtidos foram discutidos em função de duas energias de soldagem definidas em 2,0 kJ/mm e 1,0kJ/mm. A variação do insumo de calor teve como propósito aumentar a taxa de resfriamento e, consequentemente, aumentar a restrição do teste, induzindo ao trincamento a frio na junta soldada. Também foram avaliados o teor de hidrogênio residual, a microestrutura e a dureza resultantes. Neste trabalho concluiu-se que, apesar do alto teor de hidrogênio residual encontrado, da elevada taxa de resfriamento imposta durante o processo de soldagem e da presença de microestrutura suscetível, não foi observada a formação de trincas nos corpos de prova. Estes resultados foram atribuídos a inadequação do teste TEKKEN sobre o estudo da suscetibilidade ao trincamento do aço API X80. / Abstract: In the development of this work was used the self-restraint TEKKEN test with the purpose to adequate this test for the evaluation of the cracking in the welded joint of API X80 steel. The Flux Cored Arc Welding (FCAW) process and the cored wires E71T-1 and E 71T8-K6 were used for the accomplishment in the welds of API X80 steel. The experimental were carried out with a factorial design 23 (PF); the input variables studied were: preheat temperature, the wire cored kind and the groove kind of the test. The output variable was always the presence of cracking in the weld joint. The results obtained were discussed in function of two heat input defined in: 2,0 kJ/mm and 1,0kJ/mm. The variation of the heat input was have the purpose of increase the cooling rate and, consequently increased the restraint of the test, to induced cold cracking in the weld joint. It was also evaluated the content of residual hydrogen, the microstructure and the hardness obtained. In this work can be concluded that, in the spite of, high content of residual hydrogen founded, and the high cooling rate, during the welding and the presence of susceptibility microstructure was not observed the formation of cracks in the test pieces. These results were attributed to the inadequate TEKKEN test over the susceptibility cracking API X80 steel studied. / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/265306 |
| Date | 15 August 2018 |
| Creators | Perea Corimaya, Rodrigo Luis |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Trevisan, Roseana da Exaltação, 1951-, Zoqui, Eugênio José, Fals, Hipolito Carvajal |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 93 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds