Orientadores: Elizabete Jordão, Mario de Jesus Mendes / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-07-21T01:53:56Z (GMT). No. of bitstreams: 1
Silva_AntonioBeneditoda_D.pdf: 3879998 bytes, checksum: 292f843237b2727c3737ad17547c83cf (MD5)
Previous issue date: 1995 / Resumo: Neste estudo foram desenvolvidos catalisadores à base de Pt suportados em Carvão e Óxido de Titânio e promovidos com Fe e Sn, com vistas à utilização na reação de hidrogenação do aldeído cinâmico a álcool cinâmico. Os catalisadores com a seguinte composição (p/p): 5% Pt, 4,7% Pt - 0,3% Fe and 4,16% Pt - 0,84% Sn foram preparados pelo método da coimpregnação. A pré-redução dos catalisadores suportados em Carvão foi feita a 430°C, já os suportados em Óxido de Titânio tiveram sua temperatura de pré-redução identificada pelos perfis de TPR. A redução "in situ" foi realizada a 60°C, sob pressão de 4 MPa, durante 2h, para todos os referidos catalisadores. A caracterização tisico-química dos catalisadores envolveu os seguintes métodos: Difração de Raios X (XRD), Redução à Temperatura Programada (TPR), Microscopia Eletrônica de Varredura e Área Superficial (BET). Os testes catalíticos na reação de hidrogenação do aldeído cinâmico em fase líquida, a 60°C e pressão de hidrogênio de 4MPa, foram conduzidos usando-se como solvente uma mistura de álcool isopropílico e solução de acetato de sódio 0,1 N. Os resultados dos testes catalíticos revelaram que o emprego de Óxido de Titânio como suporte elevou significativamente a seletividade da reação aálcool cinâmico, enquanto que a adição de Fe aumentou substancialmente a atividade da referida reação / Abstract: The selective hydrogenation of cinnamaldehyde to cinnamic alcohol in the liquid phase was investigated over a series of catalysts based on platinum, supported on activate carbon and titanium dioxide, promoted with Fe and Sn. The catalysts with the following composition: 5% Pt, 4.7% Pt - 0.3% Fe and 4.16% Pt-0.84% Sn were prepared by co-impregnation. The catalysts supported on activated carbon were reduced at 430°C, while the ones supported on titanium dioxide were pre-reduced at different temperatures based on TPR (Temperature Programmed Reduction) experiments. The activation of the catalysts was done "in situ" over 2 hours under reaction conditions. The characterization of the catalysts was done by TPR, Electronic Scanning Microscopy, X-Ray Diffraction and Surface Area (BET). Catalytic tests of the reaction of hydrogenation of cinnamaldehyde in the liquid phase were conducted under 60°C, hydrogen pressure of 4 MPa, using isopropanol and sodium acetate 0.1 N solution as a solvent. The results of the catalytic test showed that the use of titanium dioxide as a support increased significantly the selectivity of cinnamyl alcohol compared to the same catalysts supported on carbono The addition of Fe increased significantly the activity of the hydrogenation of cinnamaldehyde / Doutorado / Sistema de Processos Quimicos e Informatica / Doutor em Engenharia Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266322 |
| Date | 29 June 1995 |
| Creators | Silva, Antonio Benedito da |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Mendes, Mario de Jesus, 1938-, Jordão, Elizabete, 1956-, Galembeck, Fernando, Buffon, Regina, Cobo, Antonio Jose Gomez, Pereira, João Alexandre Ferreira da Rocha |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 125f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds