Orientador: Marco-Aurelio De Paoli / Tese (Doutorado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-10T02:43:20Z (GMT). No. of bitstreams: 1
Vallim_MarcioRoberto_D.pdf: 1739419 bytes, checksum: ccd0a1bb0b8347580c6c5296c09efe30 (MD5)
Previous issue date: 2007 / Resumo: Blendas poliméricas, geralmente, são imiscíveis, devido à baixa entropia de mistura, e incompatíveis, devido à ausência de interações intermoleculares entre as fases, resultando em propriedades mecânicas inadequadas. O uso de copolímeros bloco ou de enxertia é uma forma de promover a adesão entre as fases e reduzir a tensão interfacial. Neste trabalho foi estudado o efeito da substituição do polietileno de alta densidade pelo polietileno de alta densidade pós-consumo (PEpc) em blendas com a poliamida-6 (PA6), a fim de verificar se o PEpc age como um compatibilizante. As blendas foram preparadas nas composições de 25, 50 e 75 % em massa de PA6, usando extrusora mono- ou dupla-rosca com perfil de temperatura de 230 a 255 °C a 102 rpm. Os ¿espaguetes¿ foram resfriados em banho d¿água, picotados e, posteriormente, injetados com o mesmo perfil de temperatura e os corpos de prova foram resfriados no molde a 20 °C por 20 s. A microscopia eletrônica de varredura das fraturas criogênicas revelou uma redução no diâmetro médio da fase dispersa das blendas contendo PEpc e os ensaios mecânicos mostraram que ocorreram aumentos da tensão na força máxima, do módulo de flexão e da resistência ao impacto. Por outro lado, a estabilidade térmica (temperatura inicial de degradação e temperatura de máxima velocidade de degradação) e as propriedades térmicas (entalpia de fusão e temperaturas de fusão e de cristalização) não sofreram alteração significativa. A hipótese da interação entre o PEpc e a PA6 foi reforçada pela aplicação dos dados de viscosidade aparente dos homopolímeros ao modelo empírico de Wu, pela formação de suspensão coloidal estável durante o teste de Molau e pelo aumento do módulo de armazenamento, verificado pela análise dinâmico-mecânica. Conclui-se que os grupos polares resultantes da degradação da cadeia do PEpc interagem quimicamente com a PA6, desempenhando um efeito compatibilizante, o qual, resulta em redução da tensão interfacial e aumento da adesão entre as fases da blenda / Abstract: Polymer blends are commonly immiscible, due to the small entropy of mixture, and incompatible, caused by the absence of intermolecular interactions between the phases, resulting in poor mechanical properties. The addition of block or graft copolymers is an alternative way to improve the adhesion at the interface and to reduce the interfacial tension. In this work, high density polyethylene or post-consumer high density polyethylene (PEpc) were blended with polyamide-6 (PA6) to verify the supposed compatibilizing effect of PEpc. Blends were prepared with 25, 50 and 75 wt % of PA6, by using a single- or a twin-screw extruder, at a temperature range from 230 to 255 °C and 102 rpm rotational speed. Test specimens were obtained by injection molding at the same conditions of the extrusion. The temperature and the period of molding were 20 °C and 20 s, respectively. The scanning electron microscopy showed a reduction in the size domains of the disperse phase when PEpc was used, in addition the tensile strength, the flexural modulus and the impact strength were improved. The thermal stability (onset degradation temperature and maximum degradation temperature) and the thermal properties (melting and crystallization temperatures and fusion enthalpy) were unaffected by PEpc. The hypothesis of the compatibilizing effect of PEpc was supported by the simulation for domain size using the Wu equation, by the formation of a colloidal suspension in the Molau test and by the increase of storage modulus in the dynamic-mechanical analysis. It could be concluded that PEpc acts as a compatibilizer in PA6 blends, decreasing the interfacial tension and improving the phase adhesion, by the interaction of the amine end groups of PA6 and the polar groups of PEpc, generated from its environmental and thermomechanical degradation / Doutorado / Físico-Química / Doutor em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/248657 |
| Date | 19 December 2007 |
| Creators | Vallim, Marcio Roberto |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, De Paoli, Marco-Aurelio, 1949-, Paoli, Marco-Aurelio De, Junior, Sebastião Vicente Canevarolo, Wiebeck, Helio, Gonçalves, Maria do Carmo, Felisberti, Maria Isabel |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Ciências |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 77p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |