<p dir="ltr">A current engineering challenge is to understand and validate material systems capable of maintaining structural viability under the elevated temperature and environmental conditions of hypersonic flight. One aspect of this challenge is the joining of multiple materials with thermal expansion mismatch, which can lead to residual stress, resulting in debits in component lifetime under in-service loading. The focus of this work is a series of studies focused on a ceramic-metal composite (WC/Cu), a zirconia coating applied to a carboncarbon (C/C) composite, and a silicide (R512E) coating applied to a Nb-based alloy (C103). Each of these material systems are candidates for elevated temperature applications in which dissimilar constituents result in residual stress in the material. Each study leveraged experimental residual strain measurements, with the primary focus on the use of synchrotron X-ray diffraction, in conjunction with representative models, and microscopy to illuminate the active mechanisms in the development and evolution of residual stress in the bulk material. The combination of experimental and modeling predictions provides a framework to inform the viability and lifing of material systems exhibiting dissimilar expansion properties.</p>
| Identifer | oai:union.ndltd.org:purdue.edu/oai:figshare.com:article/24747525 |
| Date | 10 December 2023 |
| Creators | John I Ferguson (17582760) |
| Source Sets | Purdue University |
| Detected Language | English |
| Type | Text, Thesis |
| Rights | CC BY 4.0 |
| Relation | https://figshare.com/articles/thesis/RESIDUAL_STRESS_AND_MICROSTRUCTURAL_EVOLUTION_OF_COMPOSITES_AND_COATINGS_FOR_EXTREME_ENVIRONMENTS/24747525 |
Page generated in 0.0018 seconds