This thesis deals with a high temperature testing of fracture toughness and studies the size effect on measured values using miniature size CT specimen. Two types of specimen geometry were manufactured from P91 steel, the standard size and the quarter size specimen. J-R curves were obtained in the temperature range from 23°C to 600°C. No specimen size effect was observed at room temperature tests. The realized experiments together with fractography analysis demonstrated the drop of toughness at 400°C caused by the effect of dynamic strain aging.