The main content of this master's thesis is a determination of the fatigue properties by using non-destructive testing methods – the acoustic emission technique and the X-ray diffraction. The reactor steel, that is named GOST 15Ch2NMFA, is used as a model material and is used to manufacture VVER-1000 reactor pressure vessels. The supplied material was made of two different steel melting, designated as H and S. For the basic measurement of the fatigue properties the stress-cycle asymmetry R = -1 was used. Some of the samples were used for approximate determination of the fatigue strength stress-cycle asymmetry R = 0. During the loading process the resonance frequency of the loading machine and acoustic emission signals were recorded. The changes in microstructure were estimated from the record of acoustic emissions during the whole fatigue life. The change of the microstructure was experimentally observed by X-ray diffraction analysis. The mechanism of the fatigue can be described by the observation of the microstructural processes as well as the relevant bifurcation with sufficient sensitivity. The results of the used methods indicate a decay and re-growth of mosaic blocks during the whole loading process. Therefore, it is important to find a correlation of these two non-destructive methods, or to use other non-destructive testing methods in the future.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:231140 |
| Date | January 2014 |
| Creators | Horník, Vít |
| Contributors | Mazal, Pavel, Věchet, Stanislav |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0019 seconds